2009, Vol. 26(6): 66105-066105    DOI: 10.1088/0256-307X/26/6/066105
Effect of Yttrium Addition on Glass Forming Ability of ZrCuAlSi Alloy
ZHANG Bao-Qing1,2, ZHANG Xin-Yu1, LI Gong1, SUN Bao-Ru1, FAN Chang-Zeng1, ZHAN Zai-Ji1, LIU Ri-Ping1, WANG Wen-Kui1
1State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 0660042School of Material Science and Engineering, Henan Polytechnic University, Jiaozuo 454000
收稿日期 2009-01-04  修回日期 1900-01-01
Supporting info

[1] Cao Q P, Li J F and Zhou Y H 2008 Chin. Phys. Lett.
25 3459

[2] Inoue A and Takeuchi A 2002 Mater. Trans. 43
1892

[3] Inoue A 2000 Acta Mater. 48 279

[4] Kui H W, Greer A L and Turnbull D 1984 Appl. Phys.
Lett. 45 615

[5] Yokoyama Y, Fukaura K and Inoue A 2004 Mater. Sci.
Eng. A 375 427

[6] Zhang Q S, Zhang W and Inoue A 2006 Scripta Mater.
55 711

[7] Eckert J, Das J, Kim K B, Baier F, Tang M B, Wang W H and
Zhang Z F 2006 Intermetallics 14 876

[8] Wang D, Tan H and Li Y 2005 Acta Mater. 53
2969

[9] Wang W H, Dong C and Shek C H 2004 Mater. Sci. Eng.
R 44 45

[10] Yu P, Bai H Y and Wang W H 2006 J. Mater. Res.
21 7

[11] Zhang B Q et al 2009 J. Alloys Compd. 468 187

[12] Inoue A, Zhang T 1999 Non-Cryst. Solids 252
552

[13] Turnbull D 1969 Contemp. Phys. 10 473

[14] Lu Z P and Liu CT 2002 Acta Mater. 50 3501