Passively Q-Switched Yb-Doped Fiber Laser Operating at 1.06μm with Two-Dimensional Silver Nanoplate as Saturable Absorber
Sheng-Gui Fu** , Xue-Ying Ouyang, Jin-Jian Li, Xiao-Juan Liu
School of Science, Shandong University of Technology, Zibo 255049
Abstract :A two-dimensional silver nanoplate is prepared with the seed-mediated growth method and is used for achieving pulse fiber laser operation. By controlling the dimension parameters of the silver nanoplate, the surface plasmon resonance absorption peak of the material is successfully adjusted to 1068 nm. Based on the silver nanoplate as a saturable absorber, a passively Q-switched Yb-doped fiber laser operating at 1062 nm is demonstrated. The maximum average output power of 3.49 mW is obtained with a minimum pulse width of 1.84 μs at a pulse repetition rate of 65.7 kHz, and the corresponding pulse energy and peak power are 53.1 nJ and 28.8 mW, respectively.
收稿日期: 2016-10-31
出版日期: 2017-03-21
[1] Zhang L, Li C Y, Feng B H, Wei Z Y, Li D H, Fu P M and Zhang Z G 2005 Chin. Phys. Lett. 22 1420 [2] Xue Q H, Zheng Q, Bu Y K and Qian L S 2004 Chin. Opt. Lett. 2 708 [3] Paschotta R, Häring R, Gini E, Melchior H, Keller U, Offerhaus H L and Richardson D J 1999 Opt. Lett. 24 388 [4] Popa D, Sun Z, Hasan T, Torrisi F, Wang F and Ferrari A C 2011 Appl. Phys. Lett. 98 073106 [5] Sobon G, Sotor J, Jagiello J, Kozinski R, Librant K, Zdrojek M, Lipinska L and Abramski K M 2012 Appl. Phys. Lett. 101 241106 [6] Liu J, Wu S, Yang Q H and Wang P 2011 Opt. Lett. 36 4008 [7] Kassani S H, Khazaeizhad R, Jeong Nazari T, Yeom D I and Oh K 2015 Opt. Mater. Express 5 373 [8] Chen B H, Zhang X Y, Wu K, Wang H, Wang J and Chen J P 2015 Opt. Express 23 26723 [9] Zhang M, Howe R C, Woodward R I, Edmund K J, Felice T, Hu G H, Popov V and Taylor J R 2015 Nano Res. 8 1522 [10] Mao D, Wang Y D, Ma C J, Han L, Jiang B Q, Gan X T, Hua S J, Zhang W D, Mei T and Zhao J L 2015 Sci. Rep. 5 7965 [11] Chen Y, Jiang G B, Chen S Q, Guo Z N, Yu X F, Zhao C J, Zhang H, Bao Q L, Wen S C, Tang D Y and Fan D Y 2015 Opt. Express 23 12823 [12] Yu Z H, Song Y R, Tian J R, Dou Z Y, Guoyu H Y, Li K X, Li H W and Zhang X P 2014 Opt. Express 22 11508 [13] Tang P, Zhang X, Zhao C J, Wang Y, Zhang H, Shen D Y, Wen S C, Tang D Y and Fan D Y 2013 IEEE Photon. J. 5 1500707 [14] Kang Z, Xu Y, Zhang L, Jia Z, Liu L, Zhao D and Qin W 2013 Appl. Phys. Lett. 103 041105 [15] Jiang T, Xu Y, Tian Q, Liu L, Kang Z, Yang R, Qin W 2012 Appl. Phys. Lett. 101 151122 [16] Fan D F, Mou C B, Bai X K, Wang S F, Chen N and Zeng X L 2014 Opt. Express 22 18537 [17] Zhang H N and Liu J 2016 Opt. Lett. 41 1150 [18] Kim K H, Griebner U and Herrmann J 2012 Opt. Lett. 37 1490 [19] Link S, Burda C, Mohamed M B, Nikoobakht B and El-Sayed M A 2000 Phys. Rev. B 61 6086 [20] Rao W, Li Q, Wang Y, Li T and Wu L 2015 ACS Nano 9 2783 [21] Li Q, Zhuo X, Li S, Ruan Q, Xu Q H and Wang J 2015 Adv. Opt. Mater. 3 801
[1]
. [J]. 中国物理快报, 2023, 40(2): 24201-.
[2]
. [J]. 中国物理快报, 2022, 39(2): 24201-.
[3]
. [J]. 中国物理快报, 2021, 38(9): 94201-.
[4]
. [J]. 中国物理快报, 0, (): 64202-.
[5]
. [J]. 中国物理快报, 2020, 37(6): 64202-.
[6]
. [J]. 中国物理快报, 2019, 36(10): 104202-.
[7]
. [J]. 中国物理快报, 2019, 36(7): 74203-.
[8]
. [J]. 中国物理快报, 2019, 36(5): 54202-.
[9]
. [J]. 中国物理快报, 2018, 35(11): 114202-.
[10]
. [J]. 中国物理快报, 2018, 35(11): 114203-.
[11]
. [J]. 中国物理快报, 2018, 35(10): 104201-.
[12]
. [J]. 中国物理快报, 2018, 35(8): 84201-.
[13]
. [J]. 中国物理快报, 2018, 35(5): 54201-.
[14]
. [J]. 中国物理快报, 2018, 35(4): 44201-.
[15]
. [J]. 中国物理快报, 2018, 35(4): 44204-.