Phase Transition and Negative Thermal Expansion Property of ZrMnMo$_{3}$O$_{12}$
Xiang-Hong Ge1,2, Yan-Chao Mao1, Lin Li1, Li-Ping Li1, Na Yuan1, Yong-Guang Cheng1, Juan Guo1, Ming-Ju Chao1, Er-Jun Liang1**
1College of Physical Science and Engineering, Key Laboratory of Materials Physics (Ministry of Education), Zhengzhou University, Zhengzhou 450052 2Zhongyuan University of Technology, College of Science, Zhengzhou 450007
Abstract:A novel material of ZrMnMo$_{3}$O$_{12}$ with negative thermal expansion is presented. The phase transition temperature and coefficient of thermal expansion (CTE) are investigated by temperature-dependent x-ray diffraction and Raman spectra. It is shown that ZrMnMo$_{3}$O$_{12}$ adopts monoclinic structure with space group $P21/a$ (No. 14) from 298 to 358 K and transforms to orthorhombic with space group $Pnma$ (No. 62) above 363 K. The linear CTE obtained from the results of XRD refinement is $-2.80\times10^{-6}$ K$^{-1}$ from 363 to 873 K. The CTE of the bulk cylinder ceramic measured by a thermal dilatometer is $-4.7\times10^{-6}$ K$^{-1}$ from 373 to 773 K approximatively.
Azuma M, Chen W T, Seki H, Czapski M, Olga S, Oka K, Mizumaki M, Watanuki T, Ishimatsu N, Kawamura N, Ishiwata S, Tucker M G, Shimakawa Y and Attfield J P 2011 Nat. Commun.2 234
[13]
Chen J, Wang F F, Huang Q Z, Hu L, Song X P, Deng J X, Yu R B and Xing X R 2013 Sci. Rep.3 2458