Abstract:Single crystals of pure SnS, indium (In) and antimony (Sb) doped SnS are grown by the direct vapor transport technique. Two doping concentrations of 5 at.% and 15 at.% are employed for both In and Sb dopants. In total, five samples are studied, i.e., pure SnS, 5 at.% In-doped SnS, 15 at.% In-doped SnS, 5 at.% Sb-doped SnS and 15 at.% Sb-doped SnS single crystals. The energy dispersive analysis of x-ray (EDAX) and x-ray diffraction (XRD) analysis show that all the five as-grown single crystal samples possess near perfect stoichiometry and orthorhombic structure, respectively. The doping of In and Sb in SnS is established from the EDAX data and from the shift in the peak positions in XRD. Photoelectrochemical (PEC) solar cells are fabricated by using the as-grown single crystal samples along with iodine/iodide electrolytes. Mott–Schottky plots for different compositions of iodine/iodide electrolytes show that 0.025 M I2+1 M NaI+2 M Na2SO4+0.5 M H2SO4 will be the most suitable electrolyte. Study of efficiency (η) and fill factor for different intensities of illuminations at room temperature is carried out for the five samples. The In-doped SnS single crystals show better PEC efficiency than the undoped and Sb-doped SnS single crystals.
. [J]. 中国物理快报, 2014, 31(10): 106102-106102.
Sunil H. Chaki, Mahesh D. Chaudhary, M. P. Deshpande. Effect of Indium and Antimony Doping on SnS Photoelectrochemical Solar Cells. Chin. Phys. Lett., 2014, 31(10): 106102-106102.
[1] Pass S, Chaudhary Y S, Agarwal M, Shrivastav A, Shrivastav R and Satsangi V R 2004 Ind. J. Phys.78A 229 [2] Chandra Babu K S, Srivastava O N and Subba Rao G V 1994 Curr. Sci.66 715 [3] Licht S 2001 J. Phys. Chem. B 105 6281 [4] Lewis N S 2005 Inorg. Chem.44 6900 [5] Chao J, Xie Z, Duan X, Dong Y, Wang Z, Xu J, Liang B, Shan B, Ye J, Chen D and Shen G 2012 CrystEngComm14 3163 [6] Frese K W Jr 1982 Appl. Phys. Lett.40 275 [7] Koteeshwara Reddy N, Hahn Y B, Devika M, Sumana H R and Gunasekhar K R 2007 J. Appl. Phys.101 093522 [8] Burton L A and Walsh A 2013 Appl. Phys. Lett.102 132111-1 [9] Ristov M, Sinadinovski G, Groydanov I and Mitreki M 1989 Fizika21 320 [10] Albers W, Haas C, Vink H J and Wasscher J D 1961 J. Appl. Phys.32 2220 [11] Devika M, Reddy N K, Ramesh K, Gunasekhar K R, Gopal E S R and Reddy K T R 2006 J. Electrochem. Soc.153 G727 [12] Gordillo G, Boteroa M and Oyola J S 2008 Microelectron. J.39 1351 [13] Yuying G, Weimin S and Guangpu W 2007 Proc. ISES Sol. World Congress 2007 Solar Energy and Human Settlement (Beijing, China 18–21 September 2007) p 1337 [14] Akkari A, Reghima M, Guasch C and Kamoun-Turki N 2012 J. Mater. Sci.47 1365 [15] Reghima M, Akkari A, Guasch C and Kamoun-Turki N 2012 J. Renew. Sustain. Energy4 011602 [16] Sinsermsuksakul P, Chakraborty R, Kim S B, Heald S M, Buonassisi T and Gordon R G 2012 Chem. Mater.24 4556 [17] Chaudhury M D 2014 Ph. D. Thesis (Sardar Patel University, Gujarat, India) [18] Elango M, Gopalakrishnan K, Vairam S and Thamilselcan M 2012 J. Alloys Compd.538 48 [19] Subramanian B, Sanjeeviraja C and Jayachandran M 2001 Mater. Chem. Phys.71 40 [20] Chaki S H, Agarwal M K and Patel P D 1997 Ind. J. Pure Appl. Phys.35 598 [21] Rouxel J 1979 Mater. Res. Bull.14 1425