Abstract：The temperature, duration, activation energy, and Avrami exponent of the solid phase transformation β1→α+β2 of TC4 titanium alloy treated at 3 GPa in a cooling process are calculated by means of differential scanning calorimetric curves. Then the effects of high pressure on the β1→α+β2 phase transformation dynamics of TC4 alloy in a cooling process are investigated. The results show that 3 GPa high pressure treatment can increase the activation energy of the TC4 alloy. The beginning time, end time, and duration of the β1→α+β2 phase transition of the 3 GPa high pressure treated TC4 alloy at the cooling rate of 10°C/min are increased by 2.90°C, 7.78°C and ?29.28 s respectively. It is known that 3 GPa high pressure treatment has little effect on the phase transition mechanism.
. [J]. Chin. Phys. Lett., 2013, 30(3): 36202-036202.
WANG Hai-Yan, CHEN Yan, LIU Jian-Hua, WANG Wen-Kui. Effects of 3 GPa High Pressure Treatment on the β1→α+β2 Phase Transition Dynamics of TC4 Titanium Alloy. Chin. Phys. Lett., 2013, 30(3): 36202-036202.
[1] Nyakana S L, Fanning J C and Boyer R R 2005 J. Mater. Eng. Perform.14 7991 [2] Yu S N, Wu H H, Chen G Y, Yuan X and Li Y 2011 Acta Phys. Sin.60 028104 (in Chinese) [3] Semiatin S L and Poteet P S 2008 Metall. Mater. Trans. A 39 2538 [4] Peng X N, Guo H Z, Wang T and Yao Z K 2012 Mater. Sci. Eng. A 533 55 [5] Wang H Y, Liu J H, Peng G R and Wang W K 2010 Chin. Phys. B 19 096203 [6] Jiang S, Bai L G, Liu J, Xiao W S, Li X D, Li Y C, Tang L Y, Zhang Y F, Zhang D C and Zheng L R 2009 Chin. Phys. Lett.26 076101 [7] Ming X, Wang X L, Du F, Chen G, Wang C Z and Yin J W 2012 Acta Phys. Sin.60 97102 (in Chinese) [8] Sun B R, Zhan Z J, Liang B, Zhang R J and Wang W K 2012 Chin. Phys. B 21 056101 [9] Pushin V G, Kuranova N N, Kourov N I, Valiev R Z, Valiev E Z, Makarov V V, Pushin A V and Uksusnikov A N 2012 Tech. Phys.57 1106 [10] Manoun B, Saxena S K and Barsoum M W 2005 Appl. Phys. Lett.86 101906 [11] Chen Y, Li Y L, Liu J H and Zhang R J 2012 Acta Phys. Sin.61 196203 (in Chinese) [12] Ozawa T 1971 Polymer12 150 [13] Zhang Z, Wang Q J and Mo W 2009 Metallography and Heat Treatment of Titanium (Beijing: Metallurgical Industry Press) (in Chinese) [14] Wang Y H, Liao B, Liu J H, Chen S Q, Feng Y, Zhang Y Y and Zhang R J 2012 Phase Transit.85 650 [15] Sinha I and Mandal R K 2011 J. Non-Cryst. Solids357 919
2013, Vol. 30 