摘要The local magnetic and electronic structures of chromium substituted iron oxide polycrystalline samples are investigated via Fe L-edge x-ray absorption near-edge structural and magnetic circular dichroism measurements. A strong dependence of atomic magnetic levels on the applied external magnetic field is observed. The magnetic behavior of Cr-doped iron oxides are determined to be dominantly governed by the d–d hybridization between Fe and Cr valence levels. In addition, the formation of CrO2 and Cr2O3 chromium oxide clusters in the sample are observed to determine the magnetic ordering, i.e. anti-ferromagnetic or ferromagnetic with the changing external magnetic fields. The results highly agree with the previous studies.
Abstract：The local magnetic and electronic structures of chromium substituted iron oxide polycrystalline samples are investigated via Fe L-edge x-ray absorption near-edge structural and magnetic circular dichroism measurements. A strong dependence of atomic magnetic levels on the applied external magnetic field is observed. The magnetic behavior of Cr-doped iron oxides are determined to be dominantly governed by the d–d hybridization between Fe and Cr valence levels. In addition, the formation of CrO2 and Cr2O3 chromium oxide clusters in the sample are observed to determine the magnetic ordering, i.e. anti-ferromagnetic or ferromagnetic with the changing external magnetic fields. The results highly agree with the previous studies.
Osman Murat Ozkendir**. Chromium Substitution Effect on the Magnetic Structure of Iron Oxides[J]. 中国物理快报, 2012, 29(5): 57502-057502.
Osman Murat Ozkendir**. Chromium Substitution Effect on the Magnetic Structure of Iron Oxides. Chin. Phys. Lett., 2012, 29(5): 57502-057502.
2012, Vol. 29 