Processing YCo5 Permanent Magnetic Submicron Flakes by Surfactant-Assisted High-Energy Ball Milling
ZHANG Jing-Jing,GAO Hong-Mei,YAN Yu,BAI Xue,WANG Wen-Quan,SU Feng,DU Xiao-Bo**
State key Laboratory for Superhard Materials and Department of Physics, Jilin University, Changchun 130012
Processing YCo5 Permanent Magnetic Submicron Flakes by Surfactant-Assisted High-Energy Ball Milling
ZHANG Jing-Jing,GAO Hong-Mei,YAN Yu,BAI Xue,WANG Wen-Quan,SU Feng,DU Xiao-Bo**
State key Laboratory for Superhard Materials and Department of Physics, Jilin University, Changchun 130012
摘要 YCo5 alloy is processed by surfactant−assisted high-energy ball milling. Oleic acid is used as the surfactant and is 20% of the starting powder. The resultant particles are flakes of several microns in length and width, and 20–200 nm in thickness. The flakes have significant crystallographic anisotropy and the c -axis (also easy magnetization axes) is perpendicular to the flake's surface. Maximum coercivity of 192 kA/m is obtained in the sample milled for 100 min. Excess milling results in the appearance of Fe and deteriorates the permanent magnetic properties seriously.
Abstract :YCo5 alloy is processed by surfactant−assisted high-energy ball milling. Oleic acid is used as the surfactant and is 20% of the starting powder. The resultant particles are flakes of several microns in length and width, and 20–200 nm in thickness. The flakes have significant crystallographic anisotropy and the c -axis (also easy magnetization axes) is perpendicular to the flake's surface. Maximum coercivity of 192 kA/m is obtained in the sample milled for 100 min. Excess milling results in the appearance of Fe and deteriorates the permanent magnetic properties seriously.
收稿日期: 2011-09-25
出版日期: 2012-04-30
:
75.50.Tt
(Fine-particle systems; nanocrystalline materials)
75.50.Vv
(High coercivity materials)
75.50.Ww
(Permanent magnets)
引用本文:
ZHANG Jing-Jing,GAO Hong-Mei,YAN Yu,BAI Xue,WANG Wen-Quan,SU Feng,DU Xiao-Bo**. Processing YCo5 Permanent Magnetic Submicron Flakes by Surfactant-Assisted High-Energy Ball Milling[J]. 中国物理快报, 2012, 29(5): 57501-057501.
ZHANG Jing-Jing,GAO Hong-Mei,YAN Yu,BAI Xue,WANG Wen-Quan,SU Feng,DU Xiao-Bo**. Processing YCo5 Permanent Magnetic Submicron Flakes by Surfactant-Assisted High-Energy Ball Milling. Chin. Phys. Lett., 2012, 29(5): 57501-057501.
链接本文:
https://cpl.iphy.ac.cn/CN/10.1088/0256-307X/29/5/057501
或
https://cpl.iphy.ac.cn/CN/Y2012/V29/I5/57501
[1] Strnat K J 1988 Handbook of Ferromagnetic Materials (Amsterdam: Elsevier Science Publishers) chap 4 p 131 [2] Strnat K, Hoffer G, Olson J and Ostertag W 1967 J. Appl. Phys. 38 1001 [3] Wallace W E, Craig R S, Gupta H O, Hirosawa S, Pedziwiatr A, Oswald E and Schwab E 1984 IEEE Trans. Magn. 20 1599 [4] Velu E M T, Obermyer R T, Sankar S G and Wallace W E 1989 J. Less-Common Met. 148 67 [5] Xue G, Peng L and Zhang H W 2010 Chin. Phys. Lett. 27 017501 [6] Shahzad. F, Siddiqi. S A, Im. M Y, Avallone. A, Fischer. P, Hussain. Z, Siddiqi. I and F Hellman 2010 Chin. Phys. B 19 037504 [7] Wang F, Yan Y, Yuan Z, Bai X, Du X B, Wang W Q, Su F and Jin H M 2010 Chin. Phys. Lett. 27 067503 [8] Gabay A M, Akdogan N G, Marinescu M, Liu J F and Hadjipanayis G C 2010 J. Phys.: Condens. Matter 22 164213 [9] Cui B Z, Gabay A M, Li W F, Marinescu M, Liu J F and Hadjipanayis G C 2010 J. Appl. Phys. 107 09A721 [10] Wang Y P, Li Y, Rong C B and Liu J P 2007 Nanotechnology 18 465701 [11] Yue M, Wang Y P, Poudyal N, Rong C B and Liu J P 2009 J. Appl. Phys. 105 07A708 [12] Saravanan P, Premkumar M, Singh A K, Gopalan R and Chandrasekaran V 2009 J. Alloys Compounds 480 645 [13] Akdogan N G, Li W F and Hadjipanayis G C 2011 J. Appl. Phys. 109 07A759 [14] Simeonidis K, Sarafidis C, Papastergiadis E, Angelakeris M, Tsiaoussis I and Kalogirou O 2011 Intermetallics 19 589 [15] Shen Y, Huang M Q, Higgins A K, Liu S, Horwath J C and Chen C H 2010 J. Appl. Phys. 107 09A722 [16] Knutson S J, Shen Y, Horwath J C, Barnes P and Chen C H 2011 J. Appl. Phys. 109 07A762 [17] Zheng L Y, Cui B Z and Hadjipanayis G C 2011 Acta Materialia 59 6772 [18] Zheng L Y, Gabay A M, Li W F, Cui B Z and Hadjipanayis G C 2011 J. Appl. Phys. 109 07A721 [19] Poudyal N, Nguyen V V, Rong C B and Liu J P 2011 J. Phys. D: Appl. Phys. 44 335002 [20] Cui B Z, Li W F and Hadjipanayis G C 2011 Acta Materialia 59 563 [21] Cui B Z, Zheng L Y, Waryoba D, Marinescu M and Hadjipanayis G C 2011 J. Appl. Phys. 109 07A728 [22] Rong C B, Poudyal N and Liu J P 2010 Phys. Lett. A 374 3967 [23] Zheng L Y, Cui B Z, Akdogan N G, Li W F and Hadjipanayis G C 2010 J. Alloys Compounds 504 391 [24] Akdogan N G, Hadjipanayis G C and Sellmyer D J 2009 J. Appl. Phys. 105 07A710 [25] Saravanan P, Sharma A N and Chandrasekaran V 2009 J. Magn. Magn. Mater. 321 3138 [26] Akdogan N G, Hadjipanayis G C and Sellmyer D J 2010 Nanotechnology 21 295705 [27] Daalderop G H O, Kelly P J and Schuurmans M F H 1996 Phys. Rev. B 53 14415 [28] Sánchez Ll J L, Elizalde-Galindo J T and Matutes-Aquino J A 2003 Solid State Commun. 127 527 [29] Elizalde-Galindo J T, Esparza-Ponce H, Matutes-Aquino J, Paraguay-Delgado F and Li J L S 2004 Revista Mex. Fis. 50 17 [30] Elizalde Galindo J T, Matutes-Aquino J A, Costes M and Broto J M 2006 J. Appl. Phys. 99 08B512 [31] Galindo J T E, Aquino J A M and Davies H A 2006 Int. J. Mater. Product Technol. 27 85 [32] Elizalde Galindo J T, Rivera Gómez F J and Matutes Aquino J A 2009 J. Appl. Phys. 105 07A725 [33] Kaczmarek W A and Ninham B W 1995 Mater. Chem. Phys. 40 21 [34] Guérard D 2008 Rev. Adv. Mater. Sci. 18 225 [35] Dust K D and Kronmuller H 1987 J. Magn. Magn. Mater. 68 63 [36] Martinek G and Kronmiiller H 1990 J. Magn. Magn. Mater. 86 177 [37] Givord D, Tanaud P and Viadieu T 1988 J. Magn. Magn. Mater. 72 247
[1]
. [J]. 中国物理快报, 2018, 35(2): 27501-.
[2]
. [J]. 中国物理快报, 2014, 31(2): 24701-024701.
[3]
. [J]. Chin. Phys. Lett., 2013, 30(3): 37501-037501.
[4]
LÜDong-Li;XU Chen. Magnetization Switching in a Small Disk with Shape Anisotropy [J]. 中国物理快报, 2010, 27(9): 97503-097503.
[5]
WANG Fei;YAN Yu;YUAN Zhou;BAI Xue;DU Xiao-Bo;WANG Wen-Quan;SU Feng;JIN Han-Min. Permanent Magnetic Properties of Melt-Spun YCo5 Cx Ribbons [J]. 中国物理快报, 2010, 27(6): 67503-067503.
[6]
GUO Jia-Jun;CHEN Lei;ZHAO Xu;FAN Su-Li;CHEN Wei. Effective Anisotropy in Magnetically Nd2 Fe14 B/α-Fe Nanocomposite [J]. 中国物理快报, 2010, 27(5): 57502-057502.
[7]
M. Farahmandjou;S. A. Sebt; S. S. Parhizgar;P. Aberomand;M. Akhavan. Stability Investigation of Colloidal FePt Nanoparticle Systems by Spectrophotometer Analysis [J]. 中国物理快报, 2009, 26(2): 27501-027501.
[8]
FANG Wen-Xiao;HE Zhen-Hui;CHEN Di-Hu;ZHAO Yan-E. A Diffusion Model of Field-Induced Aggregation in Ferrofluid Film [J]. 中国物理快报, 2008, 25(9): 3418-3421.
[9]
A.V. Svalov;V.O. Vas'kovskiy;G.V.Kurlyandskaya;J.M. Barandiaran;N.N. Schegoleva;A.N. Sorokin. Magnetic Behaviour of Tb/Si Nanoscale Multilayers with Small Thickness of Rare Earth Layers [J]. 中国物理快报, 2007, 24(6): 1717-1719.
[10]
BI Hong;;CHEN Qian-Wang;YOU Feng-Yong;ZHOU Xiao-Li. A Chemical Synthesis of Ferromagnetic Zn0.99 Co0.01 O Nano-Needles [J]. 中国物理快报, 2006, 23(7): 1907-1910.
[11]
A. V. Svalov;V. O. Vas’kovskiy;G. V. Kurlyandskaya;J. M. Barandiaran;I. Orue;N. N. Schegoleva;A. N. Sorokin. Structural Peculiarities and Magnetic Properties of Nanoscale Terbium in Tb/Ti and Tb/Si Multilayers [J]. 中国物理快报, 2006, 23(1): 196-199.
[12]
ZHANG Ning;BAO Jian-Chun;LI Gang;GENG Tao;CHEN Ji-Kang. Intergranular Tunnelling and Field-Induced Percolation Fluctuation of Granular Composites (La1-z Agz MnO3 )/(MnO2 /Mn2 O3 ) [J]. 中国物理快报, 2005, 22(11): 2940-2943.
[13]
FANG Wen-Xiao;HE Zhen-Hui;XU Xue-Qing;SHEN Hui. Aligned Structures of Fe3 O4 Nanoparticles in a Curable Polymer Carrier Induced by a Magnetic Field [J]. 中国物理快报, 2005, 22(9): 2386-2389.
[14]
FANG Yi-Kun;CHANG Cheng-Wu;CHANG Wen-Cheng;XIA Ai-Lin;CHEN Qiang;GE Hong-Liang;HAN Bao-Shan. Magnetic and Crystalline Microstructures of Fe--Pt--B Nanocomposite Ribbons [J]. 中国物理快报, 2005, 22(7): 1776-1779.
[15]
XU Chen;HUI Pak-Ming;CHOW Chow-Wang;LI Zhen-Ya. Switching Behaviour of Magnetic Particles with Dipolar Interaction [J]. 中国物理快报, 2005, 22(1): 211-214.