Mechanism of the Pyroelectric Response under Direct-Current Bias in La-Modified Lead Zirconate Titanate Stannate Ceramics
ZHANG Hong-Ling1, WANG Gen-Shui1, CHEN Xue-Feng1, CAO Fei1, DONG Xian-Lin1**, GU Yan2, HE Hong-Liang2, LIU Yu-Sheng2
1Key laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 2National Key Laboratory of Shock Wave and Detonation Physics, Institute of Fluid Physics, P.O. Box 919-102, Mianyang 621900
Mechanism of the Pyroelectric Response under Direct-Current Bias in La-Modified Lead Zirconate Titanate Stannate Ceramics
ZHANG Hong-Ling1, WANG Gen-Shui1, CHEN Xue-Feng1, CAO Fei1, DONG Xian-Lin1**, GU Yan2, HE Hong-Liang2, LIU Yu-Sheng2
1Key laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 2National Key Laboratory of Shock Wave and Detonation Physics, Institute of Fluid Physics, P.O. Box 919-102, Mianyang 621900
摘要Dielectric and pyroelectric properties of Pb0.97La0.02(Zr0.42Sn0.40Ti0.18)O3 ceramics are investigated as functions of temperature and dc bias field. Induced and intrinsic pyroelectric coefficients pind and p0 are calculated and analyzed. It is found that the sign, value and variation of the net pyroelectric coefficient p with increasing dc bias all are dominated by p0 under applied biases. Polarization and depolarization processes under dc biases are analyzed. Besides the contribution of pind, the diffuse and decreased pyroelectric response under dc bias compared with that of an identical field poled sample without dc bias is mainly attributed to the depolarization process under dc bias.
Abstract:Dielectric and pyroelectric properties of Pb0.97La0.02(Zr0.42Sn0.40Ti0.18)O3 ceramics are investigated as functions of temperature and dc bias field. Induced and intrinsic pyroelectric coefficients pind and p0 are calculated and analyzed. It is found that the sign, value and variation of the net pyroelectric coefficient p with increasing dc bias all are dominated by p0 under applied biases. Polarization and depolarization processes under dc biases are analyzed. Besides the contribution of pind, the diffuse and decreased pyroelectric response under dc bias compared with that of an identical field poled sample without dc bias is mainly attributed to the depolarization process under dc bias.
ZHANG Hong-Ling;WANG Gen-Shui;CHEN Xue-Feng;CAO Fei;DONG Xian-Lin**;GU Yan;HE Hong-Liang;LIU Yu-Sheng
. Mechanism of the Pyroelectric Response under Direct-Current Bias in La-Modified Lead Zirconate Titanate Stannate Ceramics[J]. 中国物理快报, 2011, 28(9): 97701-097701.
ZHANG Hong-Ling, WANG Gen-Shui, CHEN Xue-Feng, CAO Fei, DONG Xian-Lin**, GU Yan, HE Hong-Liang, LIU Yu-Sheng
. Mechanism of the Pyroelectric Response under Direct-Current Bias in La-Modified Lead Zirconate Titanate Stannate Ceramics. Chin. Phys. Lett., 2011, 28(9): 97701-097701.
[1] Watton R 1992 Ferroelectrics 133 5
[2] Hanel R A 1961 J. Opt. Soc. Am. 51 220
[3] Whatmore R W and Bell A J 1981 Ferroelectrics 35 155
[4] Whatmore R W, Osbond P C and Shorrocks N M 1987 Ferroelectrics 76 351
[5] Shorrocks N M, Whatmore R W and Osbond P C 1990 Ferroelectrics 106 387
[6] Shen M R, Yao D L and Cao W W 2005 Chin. Phys. Lett. 22 2390
[7] Jiang Y P, Tang X G, Liu Q X, Zhou Y C and Chen W L H 2008 Chin. Phys. Lett. 25 3044
[8] Hanson C, Beratan H, Owen R, Corbin M and Mckenney S 1992 Infrared Detectors: State of the Art (Bellingham: SPIE) 1735 17
[9] Jang H M and Jun Y H 1997 Ferroelectrics 193 125
[10] Zhang H L, Chen X F, Cao F, Wang G S, Dong X L, Gu Y and Liu Y S 2009 Appl. Phys. Lett. 94 252902
[11] Chan W H, Xu Z K, Zhai J W and Chen H 2005 Appl. Phys. Lett. 87 192904
[12] Zhang H L, Chen X F, Cao F, Wang G S, Dong X L, Gu Y, He H L and Liu Y S 2010 J. Appl. Phys. 108 086105
[13] Kamel T M, Kools F X N M and With G de 2007 J. Eur. Ceram. Soc. 27 2471
[14] Damjanovic D 1998 Rep. Prog. Phys. 61 1267
[15] Kim J H, Lee C H, Lee S, Lee S J and Kim S J 2009 Jpn. J. Appl. Phys. 48 101404
[16] Liu M, Hsia K J and Sardela M R 2005 J. Am. Ceram. Soc. 88 210
[17] Kounga A B, Granzow T, Aulbach E, Hinterstein M and Rodel J 2008 J. Appl. Phys. 104 024116
[18] Wu H and Shen W Z 2006 Phys. Rev. B 73 094115