摘要A novel handy single-source precursor method is adopted to prepare Gd2O2S:Yb,Ho up−conversion phosphors. Pure Gd2O2S:Yb0.06Ho0.02 phosphors are prepared via thermolysis of the air−stable ternary solid complexes RE[S2CN(C4H8)]3phen (RE=Gd, Yb, Ho) in a nitrogen atmosphere with certain amount of oxygen at 600–1100 °C. The as−prepared Gd2O2S:Yb0.06Ho0.02 exhibits a strong green up−conversion luminescence under 980 nm IR excitation. The intensity of the green emission component is 37.4 and 53.4 times more than that of the red and NIR emissions, respectively. It is indicated that the material is of excellent color purity. Under an IR excitation density of 34.75 mW/mm2 with a laser beam diameter of 1 mm, the material exhibits an up−conversion luminescence brightness of 43.68 Cd/m2.
Abstract：A novel handy single-source precursor method is adopted to prepare Gd2O2S:Yb,Ho up−conversion phosphors. Pure Gd2O2S:Yb0.06Ho0.02 phosphors are prepared via thermolysis of the air−stable ternary solid complexes RE[S2CN(C4H8)]3phen (RE=Gd, Yb, Ho) in a nitrogen atmosphere with certain amount of oxygen at 600–1100 °C. The as−prepared Gd2O2S:Yb0.06Ho0.02 exhibits a strong green up−conversion luminescence under 980 nm IR excitation. The intensity of the green emission component is 37.4 and 53.4 times more than that of the red and NIR emissions, respectively. It is indicated that the material is of excellent color purity. Under an IR excitation density of 34.75 mW/mm2 with a laser beam diameter of 1 mm, the material exhibits an up−conversion luminescence brightness of 43.68 Cd/m2.
ZHONG Hai-Yang;LUO Xi-Xian**;MA Lu-Bin;ZHANG Ming;XING Ming-Ming;FU Yao
. Preparation of Gd2O2S:Yb,Ho Phosphor via Thermolysis of Sulfur−Contained (Gd,Yb,Ho)[S2CN(C4H8)]3 Phen Complexes[J]. 中国物理快报, 2011, 28(4): 47805-047805.
ZHONG Hai-Yang, LUO Xi-Xian**, MA Lu-Bin, ZHANG Ming, XING Ming-Ming, FU Yao
. Preparation of Gd2O2S:Yb,Ho Phosphor via Thermolysis of Sulfur−Contained (Gd,Yb,Ho)[S2CN(C4H8)]3 Phen Complexes. Chin. Phys. Lett., 2011, 28(4): 47805-047805.
[1] Royce M R 1968 US Patent Specification 3418 246
[2] Ozawa L 1977 J. Electrochem. Soc. 124 413
[3] Luo X X, Cao W H and Tian Y 2007 Opt. Mater. 30 351
[4] Pitha J J, Smith A L and Ward R 1947 J. Am. Chem. Soc. 69 1870
[5] Yu S H, Han Z H, Yang J et al 1999 Chem. Mater. 11 192
[6] kuan G J, Liu Y L and Zhang J X 2005 Chem. J. Chin. Univer. 26 822
[7] Bang J, Abboudi M, Abrams B et al 2004 J. Lumin. 106 177–185
[8] Xia T, Cao W H, Luo X X et al 2005 J. Mater. Res. 20 2274
[9] Peng H S, Huang S H, You F T et al 2005 J. Phys. Chem. B 109 5774
[10] Ormond D W and Banks E 1975 J. Electrochem. Soc. 122 152
[11] Hirai T, Hirano T and Komasawa I 2002 J. Col. Interf. Sci. 253 62–69
[12] Hirai T and Orikoshi T 2004 J. Col. Interf. Sci. 273 470
[13] Hirai T and Orikoshi T 2004 J. Col. Interf. Sci. 269 103
[14] Vila L D, Stucci E B and Davolos M R 1997 J. Mater. Chem. 7 2113
[15] Luo X X, Cao W H and Xing M M 2009 J. Mater. Res. 24 1756
[16] Li S, Feindt H and Giannaras G 2002 Proc. SPIE 4809 100
[17] Pires A M, Serra O A and Davolos M R 2004 J. Alloys Compd. 374 181
[18] Boncher W L, Regulacio M D and Stoll S L 2010 Solid State Chem. 183 52
[19] Zhao F, Yuan M, Zhang W et al 2006 J. Am. Chem. Soc. 128 11758
[20] Chen S, Meng X, Xie G, Gao S and Shi Q 2006 Russ. J. Inorg. Chem. 51 445
[21] Luo X X and Cao W H 2008 J. Alloys Compd. 460 529
[22] Luo X X and Cao W H 2007 Mater. Lett. 61 3696
[23] Mai H X, Zhang Y W, Sun L D and Yan C H 2007 J. Phys. Chem. C 111 13721
2011, Vol. 28 