摘要We have prepared the β-Ga2O3 nanofibres by electrospinning method followed by calcining in air at 900°C. The morphology and structure of the nanofibres are characterized by field emission scanning electron microscopy (FE-SEM), x-ray diffraction (XRD) and Raman technique. These nanofibres have diameters ranging from 60 to 130nm and lengths up to several millimetres. Photoluminescence (PL) spectrum under excitation at 325nm shows that these β-Ga2O3 nanofibres have a blue emission peaking at 466nm, which may be attributed to defects such as the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.
Abstract：We have prepared the β-Ga2O3 nanofibres by electrospinning method followed by calcining in air at 900°C. The morphology and structure of the nanofibres are characterized by field emission scanning electron microscopy (FE-SEM), x-ray diffraction (XRD) and Raman technique. These nanofibres have diameters ranging from 60 to 130nm and lengths up to several millimetres. Photoluminescence (PL) spectrum under excitation at 325nm shows that these β-Ga2O3 nanofibres have a blue emission peaking at 466nm, which may be attributed to defects such as the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.
[1] Roy R et al 1952 J. Am. Chem. Soc. 74 719 [2] Liu Z F et al 2008 Sens. Actuators B Chem. 129666 [3] Ogita M et al 2001 Appl. Surf. Sci. 175 721 [4] Miyata T et al 2000 J. Lumin. 87-89 1183 [5] Luo L et al 2007 Appl. Phys. Lett. 90 093101 [6] Hu J Q et al 2002 J. Phys. Chem. B 106 95360 [7] Choi Y C et al 2000 Adv. Mater. 12 746 [8] Kim H W and Kim N H 2005 Appl. Phys. A 81 763 [9] Gai L G et al 2006 Nanotechnology 17 5858 [10] Sharma S and Sunkara M K 2002 J. Am. Chem. Soc. 124 12288 [11] Ma R and Bando Y 2003 Chem. Phys. Lett. 367219 [12] Doh S J et al 2008 J. Hazard. Mater. 154 118 [13] Zhan S H et al 2008 J. Colloid Interf. Sci. 318 331 [14] Li X H et al 2008 Mater. Lett. 62 2088 [15] Viswanathamurthi P et al 2003 Scripta Mater. 49 577 [16] Ye H H et al 2005 Adv. Mater. 17 1531 [17] Cui X M et al 2008 Mater. Lett. 62 1961 [18] Formalas A 1934 US patent 1975 504 () [19] Fu L et al 2003 Chem. Mater. 15 4287 [20] Rao R et al 2005 J. Appl. Phys. 98 094312 [21] Abello L et al 1998 J. Solid State Chem. 13578 [22] Katiyar R S, Dawson P, Hargreave M M and Wilknson G R1971 J. Phys. C: Solid State Phys. 4 2421 [23] Binet L and Gourier D 1998 J. Phys. Chem. Solids 59 1241 [24] Harwig T, and Kellendonk F 1978 J. Solid StateChem. 24 255 [25] Liang C H et al 2001 Appl. Phys. Lett. 783202
2008, Vol. 25 