摘要We report on ZnO nanosheets and nanorods synthesized by thermal oxidation of zinc films deposited on carbon fiber surfaces. The structure and optical properties are characterized by x-ray diffraction, scanning electron microscopy and photoluminescence spectrum. An orange-red emission around 683nm is found in the PL spectrum when the sample prepars at 400°C for four hours in air. With annealing temperature increasing from 400°C to 500°C, the blue shift is observed.
Abstract：We report on ZnO nanosheets and nanorods synthesized by thermal oxidation of zinc films deposited on carbon fiber surfaces. The structure and optical properties are characterized by x-ray diffraction, scanning electron microscopy and photoluminescence spectrum. An orange-red emission around 683nm is found in the PL spectrum when the sample prepars at 400°C for four hours in air. With annealing temperature increasing from 400°C to 500°C, the blue shift is observed.
[1] Oregan B and Gratzel M 1991 Nature 353 737 [2] Suehire J et al 2006 Nanotechnology 17 2567 [3] Bera D et al 2008 Optical mater. 30 1233 [4] Wang X D, Ding Y, Summer C J and Wang Z L 2004 JPhys. Chem. B 108 8773 [5] Wang X et al 2004 Appl. Phys. Lett. 84 4941 [6] Lee D J et al 2005 J. Cryst. Growth 276 458 [7] Tak Y and Yong K J 2005 J. Phys. Chem. B 10919263 [8] Qin Y, Wang X D and Wang Z L 2008 Nature 451809 [9] He S, Maeda H, Uehara M and Miyazaki M 2007 Mater.Lett. 61 626 [10] Wang X, Song J and Wang Z L 2006 Mater. Phys. Lett. 424 86 [11] Klingshirn C 1975 Phys. Status Solidi B 71547 [12] Umar A and Hahn YB 2006 Nanotechnology 172174 [13] Guo G S, Shi C, Tao D L, Qian W Z and Han D M 2008 J. Alloy. Compd. (in press) [14] Bai W, Zhu X, Zhu Z Q and Chu J H 2008 Appl. Surf.Sci. 254 6483 [15] Li D et al 2004 Appl. Phys. Lett. 85 1601 [16] Wu X L, Siu G G, Fu C L and Ong H C 2001 Appl. Phys.LEtt. 78 2285 [17] Zhou J G et al 2007 J. Lumin. 122/123 195 [18] Djurisic A B et al 2006 Appl. Phys. Lett. 88103107 [19] Chen S J et al 2006 J. Crystal Growth 289 55
2009, Vol. 26 