摘要PtCo/TbFeCo ferro-/ferri-exchange coupled double layer film (ECDL) was fabricated for high density magneto-optical (MO) data storage. At room temperature (RT), the PtCo film is in-plane magnetized and acts as a mask layer. However, at elevated temperature, it turns to be out-of-plane magnetized because of the strong exchange coupling interactions with the TbFeCo layer. Therefore, this ECDL film has a magnetically induced superresolution (MSR) effect. Combining it with the good Kerr signal at short wavelength, the PtCo/TbFeCo film can be a good candidate for blue laser-MSR MO data storage.
Abstract：PtCo/TbFeCo ferro-/ferri-exchange coupled double layer film (ECDL) was fabricated for high density magneto-optical (MO) data storage. At room temperature (RT), the PtCo film is in-plane magnetized and acts as a mask layer. However, at elevated temperature, it turns to be out-of-plane magnetized because of the strong exchange coupling interactions with the TbFeCo layer. Therefore, this ECDL film has a magnetically induced superresolution (MSR) effect. Combining it with the good Kerr signal at short wavelength, the PtCo/TbFeCo film can be a good candidate for blue laser-MSR MO data storage.
WANG Xian-Ying;WANG Jing;YANG Jun-He. Ferro-/Ferri-Exchange Coupled Magnetic Double Layers For High Density Magneto-optical Data Storage[J]. 中国物理快报, 2009, 26(10): 107502-107502.
WANG Xian-Ying, WANG Jing, YANG Jun-He. Ferro-/Ferri-Exchange Coupled Magnetic Double Layers For High Density Magneto-optical Data Storage. Chin. Phys. Lett., 2009, 26(10): 107502-107502.
[1] Milster T D and Curis C H 1992 Appl. Opt. 316272 [2] Masataka S, Yasuhito T, Yuuji A, Shingo I and Masayoshi K2000 Proc. SPIE 4090 160 [3] Wang X Y, Wang J, Wang Z Y and Yang J H 2008 Chin.Phy. Lett. 25 2242 [4] Yusu K, Hashimoto S and Inomata K 1992 J. Appl.Phys. 31 435 [5] Wang X Y, Zhang Y P, Li Z Y, Shen D F and Gan F X 2003 Chin. Phys. Lett. 20 135 [6] Murakami Y, Iketani N, Nakajima J, Takahashi A, Ohta K andIshikawa T 1993 J. Magn. Soc. Jpn. 17 201 [7] Zhou J, Shen D F, Yang L X, Ma B 2001 Thin SolidFilms 382 235
2009, Vol. 26 