Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH)2 Nanorods by Solution-Phase Reaction
CHENG Jin1,2,3, ZOU Xiao-Ping2,3, SONG Wei-Li4, CAO Mao-Sheng4, SU Yi2,3, YANG Gang-Qiang2,3, Lü Xue-Ming2,3, ZHANG Fu-Xue2,3
1School of Electronic Engineering, Beijing University of Posts and Telecommunications, Beijing 100876 2Research Center for Sensor Technology, Beijing Key Laboratory for Sensor, Beijing Information Science and Technology University, Jianxiangqiao Campus, Beijing 100101 3Ministry-of-Education Key Laboratory for Modern Measurement and Control Technology, Beijing 100101 4School of Material Science and Engineering, Beijing Institute of Technology, Beijing 100081
Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH)2 Nanorods by Solution-Phase Reaction
CHENG Jin1,2,3, ZOU Xiao-Ping2,3, SONG Wei-Li4, CAO Mao-Sheng4, SU Yi2,3, YANG Gang-Qiang2,3, Lü Xue-Ming2,3, ZHANG Fu-Xue2,3
1School of Electronic Engineering, Beijing University of Posts and Telecommunications, Beijing 100876 2Research Center for Sensor Technology, Beijing Key Laboratory for Sensor, Beijing Information Science and Technology University, Jianxiangqiao Campus, Beijing 100101 3Ministry-of-Education Key Laboratory for Modern Measurement and Control Technology, Beijing 100101 4School of Material Science and Engineering, Beijing Institute of Technology, Beijing 100081
We present a simple method to synthesize Pb(OH)2 nanorods by solution-phase reaction. Rod-like lead hydroxide precipitates are obtained by mixing lead nitrate with a concentration of about 0.01 M and potassium hydroxide with concentration of about 0.03 M in an aqueous solution. Sodium chloride as an additive is premixed with the lead nitrate aqueous solution. The presence of chloride ions in the precursor solution results in the rod-like morphology of lead hydroxide precipitates. The growth mechanism of the lead hydroxide nanorods is discussed.
We present a simple method to synthesize Pb(OH)2 nanorods by solution-phase reaction. Rod-like lead hydroxide precipitates are obtained by mixing lead nitrate with a concentration of about 0.01 M and potassium hydroxide with concentration of about 0.03 M in an aqueous solution. Sodium chloride as an additive is premixed with the lead nitrate aqueous solution. The presence of chloride ions in the precursor solution results in the rod-like morphology of lead hydroxide precipitates. The growth mechanism of the lead hydroxide nanorods is discussed.
CHENG Jin;;ZOU Xiao-Ping;SONG Wei-Li;CAO Mao-Sheng;SU Yi;YANG Gang-Qiang;; Lü Xue-Ming;ZHANG Fu-Xue;. Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH)2 Nanorods by Solution-Phase Reaction[J]. 中国物理快报, 2010, 27(5): 57302-057302.
CHENG Jin, , ZOU Xiao-Ping, SONG Wei-Li, CAO Mao-Sheng, SU Yi, YANG Gang-Qiang, , Lü Xue-Ming, ZHANG Fu-Xue,. Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH)2 Nanorods by Solution-Phase Reaction. Chin. Phys. Lett., 2010, 27(5): 57302-057302.
[1] Li N, Huang Y, Du F, He X B, Lin X, Gao H J, Ma Y F, Li F F, Chen Y S and Eklund P C 2006 Nano Lett. 6 1141 [2] Long Y Z, Yin Z H and Chen Z J 2008 J. Phys. Chem. C 112 11507 [3] Zhang Y, Xiang Q, Xu J Q, Xu P C, Pan Q Y and Li F 2009 J. Mater. Chem. 19 4701 [4] Long Y Z, Duvail J L, Chen Z J, Jin A Z and Gu C Z 2008 Chin. Phys. Lett. 25 3474 [5] Deng Y, Xiang Y and Song Y Z 2009 Cryst. Growth Des. 9 3079 [6] Shi X L, Cao M S, Yuan J, Zhao Q L, Kang Y Q, Fang X Y and Chen Y J 2008 Appl. Phys. Lett. 93 183118 [7] Shi X L, Cao M S, Fang X Y, Yuan J, Kang Y Q and Song W L 2008 Appl. Phys. Lett. 93 223112 [8] Che R C, Peng L M, Duan X F, Chen Q and Liang X L 2004 Adv. Mater. 16 401 [9] Song W L, Cao M S, Hou Z L, Fang X Y, Shi X L and Yuan J 2009 Appl. Phys. Lett. 94 233110 [10] Long Y Z, Zhang L J, Chen Z J, Huang K, Yang Y S, Xiao H M, Wan M X, Jin A Z and Gu C Z 2005 Phys. Rev. B 71 165412 [11] Cao M S, Shi X L, Fang X Y, Jin H B, Hou Z L, Zhou W and Chen Y J 2007 Appl. Phys. Lett. 91 203110 [12] Sheng L M, Gao W, Cao S X and Zhang J C 2008 Chin. Phys. Lett. 25 3397 [13] Shi X L, Cao M S, Yuan J and Fang X Y 2009 Appl. Phys. Lett. 95 163108 [14] Deng Y, Zhang Y J, Xiang Y, Wang G S and Xu H B 2009 J. Mater. Chem. 19 2058 [15] Liu H S, Fang X Y, Song W L, Hou Z L, Lu R, Yuan J and Cao M S 2009 Chin. Phys. Lett. 26 067101 [16] Liang H Y, Yang H X, Wang W Z, Li J Q and Xu H X 2009 J. Am. Chem. Soc. 131 6068 [17] Qiu W, Kang Y L, Lei Z K, Qin Q H and Li, Q 2009 Chin. Phys. Lett. 26 080701 [18] Wang S, Lu H J, Tu Y S, Wang C L and Fang H P 2009 Chin. Phys. Lett. 26 068702 [19] Song W L, Cao M S, Hou Z L, Yuan J and Fang X Y 2009 Scripta Mater. 61 201 [20] Li E, Cheng Z X, Xu J Q, Pan Q Y, Yu W J and Chu Y L 2009 Cryst. Growth Des. 9 2146 [21] Tao J, Lu Y H, Zheng R S, Lin K Q, Xie Z G, Luo Z F, Li S L, Wang P and Ming H 2008 Chin. Phys. Lett. 25 4459 [22] Nie C, Zhang R, Xie Z L, Xiu X Q, Liu B, Fu D Y, Liu Q J, Han P, Gu S L, Shi Y and Zheng Y D 2008 Chin. Phys. Lett. 25 1780 [23] Wang H H, Shi Y J, William C and Yigal B 2008 Chin. Phys. Lett. 25 234 [24] Feldman D G 1962 J. Cell Biol. 15 592 [25] Normann T C 1964 Stain Technol. 39 50 [26] Roach W A 1958 Annals of Botany 22 127 [27] Todd G and Parry E 1964 Nature 202 386 [28] Yurkinshii V P, Firsova E G and Petrova N V 2005 Russian J. Appl. Chem. 78 1370 [29] Perera W N, Hefter G and Sipos P M 2001 Inorg. Chem. 40 3974 [30] Sole M J and Yoffe A D 1963 Nature 198 1262 [31] Veluchamy P and Minoura H 1996 J. Mater. Sci. Lett. 15 1705 [32] Chen Z T and Gao L 2006 J. Cryst. Growth 293 522 [33] Pradhan D and Leung K T 2008 Langmuir 24 9707