Photoluminescence of C60 Single Crystals
LI Chaorong, WANG Gang, ZHANG Jiaming* , MAI Zhenhong, ZHAO Tienan, XU Lu, XIE Sishen
Institute of Physics, Academia Sinica, Beijing 100080
* Shanghai Institute of Technical Physics, Academia Sinica, Shanghai 200083
Photoluminescence of C60 Single Crystals
LI Chaorong;WANG Gang;ZHANG Jiaming* ;MAI Zhenhong;ZHAO Tienan;XU Lu;XIE Sishen
Institute of Physics, Academia Sinica, Beijing 100080
* Shanghai Institute of Technical Physics, Academia Sinica, Shanghai 200083
关键词 :
78.55.-m ,
81.10.Bk ,
61.10.-i
Abstract : The photoluminescence (PL) spectra of C60 single crystals grown under double temperature gradient (DTG) and single temperature gradient (STG) techniques were investigated at room temperature. The results show that the PL emission intensity increases first and then decreases with increasing illuminated power density for the C60 single crystals grown by both DTG and STG techniques. Furthermore, one main peak with a shoulder peak can be clearly distinguished at low illumination, while only one main peak without the shoulder peak can be seen at high illumination. The main peak undergoes a continuous blue shift and broadening with the increase of illuminated power density. The difference of PL emission energy at the same illumination density of DTG and STG samples may correlated with the degree of both the orientational disorder of C60 molecule and lattice perfectness. The Laue diffraction patterns show that the DTG sample has stronger strains and poorer crystalline quality than the STG sample.
Key words :
78.55.-m
81.10.Bk
61.10.-i
出版日期: 1995-05-01
引用本文:
LI Chaorong;WANG Gang;ZHANG Jiaming*;MAI Zhenhong;ZHAO Tienan;XU Lu;XIE Sishen
. Photoluminescence of C60 Single Crystals[J]. 中国物理快报, 1995, 12(5): 317-320.
LI Chaorong, WANG Gang, ZHANG Jiaming*, MAI Zhenhong, ZHAO Tienan, XU Lu, XIE Sishen
. Photoluminescence of C60 Single Crystals. Chin. Phys. Lett., 1995, 12(5): 317-320.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1995/V12/I5/317
[1]
YANG Jian;QIU Tai;SHEN Chun-Ying. New BCN Fibres for Strong Ultraviolet and Visible Light Luminescence [J]. 中国物理快报, 2006, 23(9): 2573-2575.
[2]
ZHU Li-Na;CHEN Xiao-Long;YANG Hui;PENG Tong-Hua;NI Dai-Qin;HU Bo-Qing. Effects of Post-Thermal Treatment on Quality of SiC Grown by PVT Method [J]. 中国物理快报, 2006, 23(8): 2273-2276.
[3]
LI Guang-Min;LI-Lan;WANG Da-Jian;ZHANG Xiao-Song;TAO Yi. Effect of Al3+ on Photoluminescence Properties of Eu3+ -Doped BaZr(BO3 )2 Phosphors [J]. 中国物理快报, 2006, 23(8): 2063-2065.
[4]
WANG Da-Jian;WANG Ji-Lei;LI Lan. Colour Tuning of Single Host Phosphors for White Light by Al Addition [J]. 中国物理快报, 2006, 23(8): 2247-2250.
[5]
DAI Shi-Xun;ZHANG Xiang-Hua;XU Tie-Feng;SHEN Xiang;WANG Xun-Shi;NIE Qiu-Hua. High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses [J]. 中国物理快报, 2006, 23(7): 1810-1812.
[6]
FANG Ying-Cui;ZHANG Zhuang-Jian;SHEN Jie;LU Ming. Photoluminescence from Electron-Beam Deposited CeO2 Thin Film after High Temperature Thermal Annealing [J]. 中国物理快报, 2006, 23(7): 1919-1922.
[7]
GUO Xing-Yuan;XU Da-Peng;DING Zhan-Hui;SU Wen-Hui;. Preparation and Raman Spectrum of Rutile Single Crystals Using Floating Zone Method [J]. 中国物理快报, 2006, 23(6): 1645-1647.
[8]
QIAN Bo;CHEN San;CEN Zhan-Hong;CHEN Kun-Ji;LIU Yan-Song;XU Jun;MA Zhong-Yuan;LI Wei;HUANG Xin-Fan. Step-by-Step Laser Crystallization of Amorphous Si:H/SiNx :H Multilayer for Active Layer in Microcavities [J]. 中国物理快报, 2006, 23(5): 1302-1305.
[9]
ZHANG Qin-Yuan; YANG Gang-Feng;JIANG Zhong-Hong;W. X. Que. Structural and Luminescence Properties of Transparent Nanocrystalline ZrO2 :Er3+ Films [J]. 中国物理快报, 2006, 23(4): 852-855.
[10]
LI Bin-Bin;XIU Xiang-Qian;ZHANG Rong;TAO Zhi-Kuo;CHEN Lin;XIE Zi-Li;ZHENG You-Dou;HE Bo/sup>. Analysis of Local Structures around Ni Atoms Doped in ZnO-Based Diluted Magnetic Semiconductors by Fluorescence EXAFS [J]. 中国物理快报, 2006, 23(4): 907-910.
[11]
SHAO Jia-Ping;HAN Yan-Jun;WANG Lai;JIANG Yang;XI Guang-Yi;LI Hong-Tao;ZHAO Wei;LUO Yi. Improved Surface Characteristics and Contact Performance of Epitaxial p-AlGaN by a Chemical Treatment Process [J]. 中国物理快报, 2006, 23(2): 432-435.
[12]
LI Xin-Hua;XU Jia-Yue;JIN Min;SHEN Hui;LI Xiao-Min. Electrical and Optical Properties of Bulk ZnO Single Crystal Grown by Flux Bridgman Method [J]. 中国物理快报, 2006, 23(12): 3356-3358.
[13]
XUE De-Sheng;GONG Yu. Abnormal Photoluminescence Properties of Polycrystalline ZnO Nanowire Arrays Synthesized by Electrodeposition [J]. 中国物理快报, 2006, 23(11): 3105-3107.
[14]
QIN Qi;GUO Li-Wei;ZHOU Zhong-Tang;CHEN Hong;DU Xiao-Long;MEI Zeng-Xia;JIA Jin-Feng;XUE Qi-Kun;ZHOU Jun-Ming. Electroluminescence of an n-ZnO/p-GaN Heterojunction under Forward and Reverse Biases [J]. 中国物理快报, 2005, 22(9): 2298-2301.
[15]
DONG Guo-Yi;ZHENG Yi-Bo;LIN Lin;DOU Jun-Hong;WEI Zhi-Ren;YANG Shao-Peng;FU Guang-Sheng;LI Xiao-Wei. Photoluminescence Mechanism of ZnO:Zn Investigated by Microwave Dielectric Spectrometry [J]. 中国物理快报, 2005, 22(8): 2092-2095.