INFLUENCE OF OXYGEN CONTENT ON SUPERCONDUCTIVITY OF Bi-SYSTEM MATERIAL
WANG Shunxi, XIA Jianshen, ZHANG Qirui, CHEN Xianhui, CHEN Zuyao, LIU Xianming, JI Mingrong
Department of Physics, University of Science and Technology of China, Hefei 230022
Department of Applied Chemistry, University of Science and Technology of China, Hefei 230022
Central lab of Structure and Element Analysis, University
of Science and Technology of China, Hefei 230022
INFLUENCE OF OXYGEN CONTENT ON SUPERCONDUCTIVITY OF Bi-SYSTEM MATERIAL
WANG Shunxi;XIA Jianshen;ZHANG Qirui;CHEN Xianhui;CHEN Zuyao;LIU Xianming;JI Mingrong
Department of Physics, University of Science and Technology of China, Hefei 230022
Department of Applied Chemistry, University of Science and Technology of China, Hefei 230022
Central lab of Structure and Element Analysis, University
of Science and Technology of China, Hefei 230022
Abstract： The sample with nominal composition Bi1.8Pb0.35Sr2Ca2Cu3Oy was prepared by solid state reaction method. Through the measurements of resistivity, dc. susceptibility, and the analysis of X-ray diffraction and Energy Dispersive X-ray (EDX) microanalysis, we found that: (1) there is only one superconducting transition with transition temperature near 110K, its zero-resistance temperature (Tce) is as high as 106.5K, the diffraction pattern is similar to that of 2223 single phase (110K), but the cation ratio of Bi:Pb:Sr:Ca:Cu is near 25.8:5.74:18.43:19.53:30.50, i.e., Bi2.5Pb0.5Sr2Ca2Cu3.We suppose that the 3223 phase is caused by intergrowth in the sample; (2) like the 1-2-3 phase material, the superconductivity of Bi-system is sensitive to oxygen content. We suppose that different oxygen content in the same crystal structure leads to the change of electronic structure, and so to great difference in the superconductivity.
(Impurity and defect levels; energy states of adsorbed species)
引用本文:
WANG Shunxi;XIA Jianshen;ZHANG Qirui;CHEN Xianhui;CHEN Zuyao;LIU Xianming;JI Mingrong. INFLUENCE OF OXYGEN CONTENT ON SUPERCONDUCTIVITY OF Bi-SYSTEM MATERIAL
[J]. 中国物理快报, 1990, 7(5): 237-240.
WANG Shunxi, XIA Jianshen, ZHANG Qirui, CHEN Xianhui, CHEN Zuyao, LIU Xianming, JI Mingrong. INFLUENCE OF OXYGEN CONTENT ON SUPERCONDUCTIVITY OF Bi-SYSTEM MATERIAL
. Chin. Phys. Lett., 1990, 7(5): 237-240.
1990, Vol. 7 