PRECIPITATION AND DEFECTS IN Nb-CONTAINING NdDyFeCoB MAGNETS
LIU Jinfang, RAO Xiaolei, ZHANG Nanning, LUO Helie
Institute of Physics, Academia Sinica, Beijing, and
San huan Corporation, Academia Sinica, Beijing
PRECIPITATION AND DEFECTS IN Nb-CONTAINING NdDyFeCoB MAGNETS
LIU Jinfang;RAO Xiaolei;ZHANG Nanning;LUO Helie
Institute of Physics, Academia Sinica, Beijing, and
San huan Corporation, Academia Sinica, Beijing
关键词 :
75.60.Gm
Abstract : The microstructure of Nb-containing NdDyFeCoB magnets has been investigated using transmission electron microscope. Very small particles whose diameters are about several to 40Å have been found in as-sintered magnets. It may be formed by self-tempering. Dislocations and stacking faults have been found inside grains. It seems that the increase of coercive field in Nb-containing magnets is closely related with defects and precipitations.
Key words :
75.60.Gm
出版日期: 1989-09-01
引用本文:
LIU Jinfang;RAO Xiaolei;ZHANG Nanning;LUO Helie. PRECIPITATION AND DEFECTS IN Nb-CONTAINING NdDyFeCoB MAGNETS[J]. 中国物理快报, 1989, 6(9): 413-416.
LIU Jinfang, RAO Xiaolei, ZHANG Nanning, LUO Helie. PRECIPITATION AND DEFECTS IN Nb-CONTAINING NdDyFeCoB MAGNETS. Chin. Phys. Lett., 1989, 6(9): 413-416.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1989/V6/I9/413
[1]
ZHANG Shao-ying;ZHANG Hong-wei;SHEN Bao-gen;ZHAN Wen-shan;CHIN Tsung-shune. Magnetic Hardening Mechanism in Nanocrystalline Sm2 Fe15-x Mx Ga2 C [J]. 中国物理快报, 1998, 15(11): 831-833.
[2]
CHENG Zhao-hua;SHEN Bao-gen;ZHANG Jun-xian;MAO Ming-xi;SUN Ji-jun;YANG Chun-li;LI Fa-shen;ZHANG Yi-de. Mössbauer Spectroscopy and X-Ray Diffraction Studies of the Phase Composition of Crystallized Ndx Fe81.5-x B18.5 Alloys with 7 ≤ x ≤15 [J]. 中国物理快报, 1997, 14(5): 387-390.
[3]
SHEN Baogen;YANG Linyuan;CAO Lei;GUO Huiqun. Magnetic Hardening of Rapidly Quenched Co-M-Zr (M=B, Fe) Alloys [J]. 中国物理快报, 1993, 10(3): 175-178.
[4]
SHEN Baogen;GUO Huiqun;YANG Linyuan;ZHAO Jian gao. A NEW PERMANENT MAGNETIC MATERIALS CRYSTALLIZED FROM AMORPHOUS Co84-x Bx Zr16 ALLOYS
[J]. 中国物理快报, 1990, 7(8): 365-368.
[5]
YANG Chunli;ZHOU Rongjie;LI Fashen;ZHONG Wending*;LAN Jian*. MAGNETIC AND 57 Fe MÖSSBAUER STUDY OF YFe12-x Vx COMPOUNDS [J]. 中国物理快报, 1990, 7(8): 373-376.
[6]
YIN Malie;HU Jifan;LIU Yinglie;WANG Zhenxi;LIN Wengui. SIMULTANEOUS INCREASE OF REMANENCE AND COERCIWTY OF Nd-Fe-B MAGNETS BY Nb ADDITION [J]. 中国物理快报, 1990, 7(7): 330-333.