Structural Relaxation of Pd39Ni10Cu30P21 Bulk Metallic Glass Under High Pressure
WANG Li-Min1, ZHAN Zai-Ji1, SUN Li-Ling1, LI Gong1,2, WANG Wen-Kui1,2
1Center for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080
2College of Material Sciences and Chemical Engineering, Yanshan University, Qinhuangdao 066004
Structural Relaxation of Pd39Ni10Cu30P21 Bulk Metallic Glass Under High Pressure
WANG Li-Min1;ZHAN Zai-Ji1;SUN Li-Ling1;LI Gong1,2;WANG Wen-Kui1,2
1Center for Condensed Matter Physics, Chinese Academy of Sciences, Beijing 100080
2College of Material Sciences and Chemical Engineering, Yanshan University, Qinhuangdao 066004
Abstract: The Pd39Ni10Cu30P21 bulk metallic glass is isothermally relaxed under various pressures. The degree of the structural relaxation is evaluated in terms of the enthalpy recovery behaviours involved in the irreversible glass transition processes by using a temperature-modulated differential scanning calarimetry technique. A roughly linear increase of the recovery enthalpy is observed within the experimental pressure range from 2.67 to 4.45 GPa, which reflects the release of the frozen-in enthalpy in the as-quenched glass with increasing relaxation pressure. The pressure dependence of the time scale of the enthalpy recovery processes is also exhibited.
WANG Li-Min;ZHAN Zai-Ji;SUN Li-Ling;LI Gong;WANG Wen-Kui;
. Structural Relaxation of Pd39Ni10Cu30P21 Bulk Metallic Glass Under High Pressure
[J]. 中国物理快报, 2001, 18(4): 567-569.
WANG Li-Min, ZHAN Zai-Ji, SUN Li-Ling, LI Gong, WANG Wen-Kui,
. Structural Relaxation of Pd39Ni10Cu30P21 Bulk Metallic Glass Under High Pressure
. Chin. Phys. Lett., 2001, 18(4): 567-569.