Structural Properties of MgB2 Superconductors with a
Critical Current Density Greater than 105A/cm2
LI Jian-Qi1, LI Long1,2, ZHOU Yu-Qing1, REN Zhi-An1, CHE Guang-Can1, ZHAO Zhong-Xian1
1National Laboratory for Superconductivity, Institute of Physics, Chinese Academy of Sciences, Beijing 100080
2Department of Physics, Ningxia University, Yinchuan 750021
Structural Properties of MgB2 Superconductors with a
Critical Current Density Greater than 105A/cm2
LI Jian-Qi1;LI Long1,2;ZHOU Yu-Qing1;REN Zhi-An1;CHE Guang-Can1;ZHAO Zhong-Xian1
1National Laboratory for Superconductivity, Institute of Physics, Chinese Academy of Sciences, Beijing 100080
2Department of Physics, Ningxia University, Yinchuan 750021
Abstract: Structural features of MgB2 superconductors prepared under different conditions have been analysed by means of transmission electron microscopy. The MgB2 crystal is identified to have a hexagonal structure with the space group of P6/mmm. Superconducting materials synthesized under a high pressure of 6 Gpa are made of regularly stacked grains as large as a few microns in sizes. Stacking faults and microstructure properties of grain boundaries either with or without impurities, appearing in a sample with the critical current density greater than 105A/cm2, have been systematically investigated.
LI Jian-Qi;LI Long;ZHOU Yu-Qing;REN Zhi-An;CHE Guang-Can;ZHAO Zhong-Xian
. Structural Properties of MgB2 Superconductors with a
Critical Current Density Greater than 105A/cm2[J]. 中国物理快报, 2001, 18(5): 680-683.
LI Jian-Qi, LI Long, ZHOU Yu-Qing, REN Zhi-An, CHE Guang-Can, ZHAO Zhong-Xian
. Structural Properties of MgB2 Superconductors with a
Critical Current Density Greater than 105A/cm2. Chin. Phys. Lett., 2001, 18(5): 680-683.