摘要The photoinduced birefringence in an azobenzene polymer is investigated at different temperatures between -20°C to 50°C. It is found that there is a peak value of photoinduced birefringence in the temperature dependence of the photoinduced birefringence under a certain pumping intensity. With the pump light in 90mW/cm2, the peak value of the photoinduced birefringence appeared at about 0°C. The effect of temperature on the photoinduced birefringence is discussed using the competition mechanism between the photoinduced reorientation and the thermal random motion.
Abstract:The photoinduced birefringence in an azobenzene polymer is investigated at different temperatures between -20°C to 50°C. It is found that there is a peak value of photoinduced birefringence in the temperature dependence of the photoinduced birefringence under a certain pumping intensity. With the pump light in 90mW/cm2, the peak value of the photoinduced birefringence appeared at about 0°C. The effect of temperature on the photoinduced birefringence is discussed using the competition mechanism between the photoinduced reorientation and the thermal random motion.
XU Hong-Tao;WANG Chang-Shun;PAN Xu; ZHANG Xiao-Qiang;WANG Chuan-Yu;SUN Cun-Ying. Temperature Dependence of Photoinduced Birefringence in an Azobenzene Polymer[J]. 中国物理快报, 2007, 24(2): 450-453.
XU Hong-Tao, WANG Chang-Shun, PAN Xu, ZHANG Xiao-Qiang, WANG Chuan-Yu, SUN Cun-Ying. Temperature Dependence of Photoinduced Birefringence in an Azobenzene Polymer. Chin. Phys. Lett., 2007, 24(2): 450-453.
[1] Sekkat Z et al 1997 J. Opt. Soc. Am. B 14 829 [2] Huang M M et al 2004 Chin. Phys. Lett. 21 1969 [3] Natansohn A and Rochon P 1999 Adv. Mater. 11 1387 [4] Hvilsted S, Andruzzi F and Ramanujam P S 1992 Opt. Lett. 17 1234 [5] Chen W Z et al 2006 Chin. Phys. Lett. 23 151 [6] Natansohn A et al 1992 Macromolecules 25 2268 [7] Buffeteau T and P\'ezolet M 1996 Appl. Spectrosc. 50 948 [8] Wang C S et al 1999 Appl. Phys. Lett. 74 19 [9] Wang C S et al 1999 Appl. Phys. B 68 1117 [10] Song O K, Wang C H and Pauley M A 1997 Macromolecules 30 6913 [11] Brown D, Natansohn A and Rochon P 1995 Macromolecules 28 6116 [12] Tawa K et al 2000 Polymer 41 3235 [13] Hwang J S, Lee G J and Lim T K 1994 J. Korean Phys. Soc. 27 392 [14] Ivanov S et al 1991 Makromol. Chem. 12 709 [15] Blanche P A et al 2000 J. Opt. Soc. Am. B 17 729 [16] Pan L Y et al 2004 J. Phys. D: Appl. Phys. 37 1002 [17] Mita I, Horie K and Hirao K 1989 Macromolecules 22 558 [18] Maertens C et al 1999 Polymer. Int. 48 205 [19] Silva J R et al 2002 Polymer 43 3753 [20] Agnol F D et al 2002 Macromol. Rapid Commun. 23 948 [21] Sch\"onhoff M, Mertesdorf M and L\"osche M 1996 J. Phys.Chem. 100 7558 [22] Ramanujam P S 2003 Opt. Lett. 28 2375 [23] Du W C and Liu S H 1993 Thin Solid Films 229 122 [24] Werner O et al 1990 Opt. Lett. 15 1117