摘要The interaction between small vacancy clusters and twin boundaries in copper is studied by using many-body potential developed by Ackland et al. for fcc metals. The interaction energies of single-, di- and tri-vacancy clusters with (111) and (112) twin boundaries are computed using well established simulation techniques. For (111) twins the vacancy clusters are highly repelled when they are on the adjacent planes, and are attracted when they are away from the boundary. In the case of (112) twins, vacancy clusters are more attracted to the boundary when they are near the boundary as compared to away from it. Vacancy clusters on both the sides of the boundary are also investigated, and it is observed that the clusters energetically prefer to lie on the off-mirror sites as compared to the mirror position across the twin.
Abstract：The interaction between small vacancy clusters and twin boundaries in copper is studied by using many-body potential developed by Ackland et al. for fcc metals. The interaction energies of single-, di- and tri-vacancy clusters with (111) and (112) twin boundaries are computed using well established simulation techniques. For (111) twins the vacancy clusters are highly repelled when they are on the adjacent planes, and are attracted when they are away from the boundary. In the case of (112) twins, vacancy clusters are more attracted to the boundary when they are near the boundary as compared to away from it. Vacancy clusters on both the sides of the boundary are also investigated, and it is observed that the clusters energetically prefer to lie on the off-mirror sites as compared to the mirror position across the twin.
S. A. Ahmad;Razia Ramzan. Interaction of Point Defects with Twin Boundaries in Copper[J]. 中国物理快报, 2007, 24(9): 2631-2634.
S. A. Ahmad, Razia Ramzan. Interaction of Point Defects with Twin Boundaries in Copper. Chin. Phys. Lett., 2007, 24(9): 2631-2634.
[1] Crocker A G 1975 Philos. Mag. 32 379 [2] Crocker A G and Faridi B A 1980 Acta Metall. 28 549 [3] Noorullah, Akhter J I and Yaldram K 1997 The Nucleus 34 17 [4] Ahmad S A, Crocker A G and Faridi B A 1983 Philos. Mag.A 48 31 [5] Merz M D, Dahlgren S D 1975 J. Appl. Phys. 46 3235 [6] Youngdahl C J et al 2001 Scripta Materialia 44 1475 [7] Wang J et al 2004 J. Phys, Chem. B 108 841 [8] Crocker A G and Faridi B A 1978 J. Nucl. Mater. 69/70 671 [9] Crocker A G and Faridi B A 1980 Acta Metall. 28 549 [10] Malik A Q and Crocker A G 1985 Philos. Mag. A 51 551 [11] Ackland G J et al %, Tichy G, Vitek V and Finnis M W1987 Philos.Mag. A 56 735 [12] Faridi B A et al %, Ahmad S A and Choudhry M A1991 Ind. J. Pure Appl.Phys. 29 796 [13] Ahmad S A et al %, Faridi B A and Choudhry M A1992 Ind. J. Pure Appl.Phys. 30 439 [14] Park H S, Gall K and Zimmerman J A 2005 Phys. Rev. Lett. 95255504 [15] Fletcher R 1972 AERE Report No R 7073
2007, Vol. 24 