Characterization of Cu-Zn Alloy Nanocrystalline Powders Prepared by Wire Electrical Explosion
WANG Qun, YANG Hai-Bin, GUO Wei-Li, ZOU Guang-Tian
National Laboratory of Superhard Materials, Jilin University, Changchun 130023
Characterization of Cu-Zn Alloy Nanocrystalline Powders Prepared by Wire Electrical Explosion
WANG Qun;YANG Hai-Bin;GUO Wei-Li;ZOU Guang-Tian
National Laboratory of Superhard Materials, Jilin University, Changchun 130023
关键词 :
81.20.-n ,
64.70.-p
Abstract : Nanocrystalline powders of Cu-Zn alloy in size ranging from 10 to 140nm was prepared from α-Cu-Zn alloy wire containing 39.8at.% Zn by an electrical explosion method. The particles are identified from x-ray diffraction as a mixture of the α, β, γ, and ε phases of Cu-Zn alloy. Most of the particles are hexagonal in shape, with only a small part being spherical and cubic. The composition of Zn in the explosion products varied from 6.9 to 45.2at.% in different particles as determined by energy dispersive x-ray spectrometer. A possible mechanism for the formation of the alloy nanocrystalline powders is proposed, in which a redistribution process occurred caused by strong collision and diffusion between the two kinds of atoms during the powder formation.
Key words :
81.20.-n
64.70.-p
出版日期: 2000-02-01
:
81.20.-n
(Methods of materials synthesis and materials processing)
64.70.-p
(Specific phase transitions)
引用本文:
WANG Qun;YANG Hai-Bin;GUO Wei-Li;ZOU Guang-Tian. Characterization of Cu-Zn Alloy Nanocrystalline Powders Prepared by Wire Electrical Explosion[J]. 中国物理快报, 2000, 17(2): 145-147.
WANG Qun, YANG Hai-Bin, GUO Wei-Li, ZOU Guang-Tian. Characterization of Cu-Zn Alloy Nanocrystalline Powders Prepared by Wire Electrical Explosion. Chin. Phys. Lett., 2000, 17(2): 145-147.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2000/V17/I2/145
[1]
SHEN Ming-Rong;YAO Dong-Lai;CAO Wen-Wu. Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955Pb(Zn1/3 Nb2/3 )O3 --0.045PbTiO3 Single Crystals [J]. 中国物理快报, 2005, 22(9): 2390-2393.
[2]
WANG Hong-Chang;WANG Zhan-Shan;ZHANG Shu-Min;WU Wen-Juan;ZHANG Zhong;GU Zhong-Xiang;XU Yao;WANG Feng-Li;CHENG Xin-Bin;WANG Bei;QIN Shu-Ji;CHEN Ling-Yan. Fabrication and Characterization of Ni Thin Films Using Direct-Current Magnetron Sputtering [J]. 中国物理快报, 2005, 22(8): 2106-2108.
[3]
GUO Li-Cong;HU Wen-Tao;HE Ju-Long;YU Dong-Li;LIU Shi-Min;LI Dong-Chun;TIAN Yong-Jun. Synthesis of Boron-Rich Cubic B(Cx N1-x ) Compounds [J]. 中国物理快报, 2005, 22(12): 3141-3143.
[4]
LI Gong;ZHANG Xin-Yu;SUN Yi-Nan;QIAN Yu-Qing;LIU Jing;LIU Ri-Ping. Compression Behaviour of Ni77 P23 Amorphous Alloy up to 30.5GPa [J]. 中国物理快报, 2005, 22(10): 2615-2617.
[5]
YANG Li-Hong;DONG Cheng;SONG Hui-Hua;GUO Juan;FU Guang-Cai. Superconductivity in LiTi2 O4 Prepared by Hybrid Microwave Method [J]. 中国物理快报, 2005, 22(1): 243-245.
[6]
LI Gong;ZHAN Zai-Ji;WANG Li-Min;SUN Li-Ling;LIU Jing;WANG Wen-Kui;. Compression Behaviour and Equation of State of Zr44.4 Nb7 Cu13.5 Ni10.8 Be24.3 Bulk Metallic Glass up to 39 GPa [J]. 中国物理快报, 2004, 21(5): 898-900.
[7]
LIU Bing;CHEN Da-Rong;CHEN Zheng;WANG Yong-Xin;LI Xiao-Ling. Effect of Electric Field on Conductivity and Vickers Hardness of an Al-Li Alloy [J]. 中国物理快报, 2003, 20(11): 2067-2069.
[8]
XIAO Chang-Ming;JIN Guo-Jun;Ma Yu-Qiang. Packing Effect of Excluded Volume on Hard-Sphere Colloids [J]. 中国物理快报, 2001, 18(7): 950-952.
[9]
XIONG Gang;MAI Zhen-Hong;WANG Chao-Ying;NI Yong-Ming;ZHAO Zhong-Xian;XU Ming;LIU Cui-Xiu;LUO Guang-Ming. Characterization of CoCrFeO4 Nanocrystals Prepared
by a Sol-Gel Method [J]. 中国物理快报, 2001, 18(5): 692-694.
[10]
CHEN Liang-Chen;WANG Li-Jun;TANG Dong-Sheng;XIE Si-Shen;JIN Chang-Qing. X-Ray Diffraction Study of Carbon Nanotubes Under High Pressure [J]. 中国物理快报, 2001, 18(4): 577-578.
[11]
ZHAO Jing;GUO Lin;LIU Jing;YANG Yang;CHE Rong-Zheng;ZHOU Lei. High Bulk Modulus of Nanocrystal γ-Fe2 O3 with Chemical Dodecyl Benzene Sulfonic Decoration Under High Pressure [J]. 中国物理快报, 2000, 17(2): 126-128.
[12]
CHEN Liang-chen;WANG Li-jun. Optical Absorption and X-Ray Diffraction Studies of Sulfur Under High Pressure [J]. 中国物理快报, 1999, 16(9): 675-676.
[13]
WANG Li-jun;CHEN Liang-chen;LI Feng-ying;GU Hui-cheng;ZHOU Lei;CHE Rong-zheng. Studies on CsBr with Synchrotron Radiation Under Ultrahigh Pressure up to 115GPa [J]. 中国物理快报, 1998, 15(4): 284-286.
[14]
CHEN Liang-chen;GU Hui-cheng;WANG Li-jun;LI Feng-ying;CHE Rong-zheng;ZHOU Lei;XIU Li-song;LAN Guo-xiang. Pressure-Induced Amorphous Transition of Li2 Ge7 O15 Crystal [J]. 中国物理快报, 1996, 13(7): 534-536.
[15]
LI Fang-hua;CHENG Yi-fan. Relationship Between Octagonal Quasicrystal and β-Mn Type Crystal in Cut Description [J]. 中国物理快报, 1996, 13(3): 199-202.