Low Field-Induced Electron Emission Phenomenon Observed from the Carbon Containing Thin Films
CHEN Jun, WEI Ai-xiang, ZHANG Hai-yan, LU Yong, ZHENG Xin-guo, MO Dang, PENG Shao-qi, XU Ning-sheng
Department of Physics, Zhongshan University, Guangzhou 510275
Low Field-Induced Electron Emission Phenomenon Observed from the Carbon Containing Thin Films
CHEN Jun;WEI Ai-xiang;ZHANG Hai-yan;LU Yong;ZHENG Xin-guo;MO Dang;PENG Shao-qi;XU Ning-sheng
Department of Physics, Zhongshan University, Guangzhou 510275
关键词 ：
79.70.+q
Abstract ： Stable cold-cathode electron emission at fields as low as 3 MV/m has been observed from two types of carbon-containing thin film of thickness in submicron scale, i. e., non-doped fullerene C60 and amorphous diamond films. A transparent anode imaging technique was used to record the spatial distribution of individual sites and the total emission current-voltage characteristic of the films. It is found that supplemental measurements of optical spectra and electrical conductivity of the films can provide important evidence useful for understanding the differences in emission behaviour between two types of film.
Key words ：
79.70.+q
出版日期: 1997-12-01
:
79.70.+q
(Field emission, ionization, evaporation, and desorption)
引用本文:
CHEN Jun;WEI Ai-xiang;ZHANG Hai-yan;LU Yong;ZHENG Xin-guo;MO Dang;PENG Shao-qi;XU Ning-sheng. Low Field-Induced Electron Emission Phenomenon Observed from the Carbon Containing Thin Films[J]. 中国物理快报, 1997, 14(12): 949-952.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1997/V14/I12/949
[1]
YONG Zhen-Zhong;GONG Jin-Long;WANG Zhen-Xia;ZHU Zhi-Yuan;HU Jian-Gang;PAN Qiang-Yan. Field Emission Enhancement of Carbon Nanotubes by Surface Modification
[2]
FU Xiao-Nan;LI Xin-Jian. Enhanced Field Emission from Well-Patterned Silicon Nanoporous Pillar Arrays
[3]
LI Zhi-Bing;WANG Wei-Liang. Analytic Solution of Charge Density of Single Wall Carbon Nanotube under Conditions of Field Electron Emission
[4]
WANG Xiao-Ping;WANG Li-Jun;ZHANG Bing-Lin;YAO Ning;ZANG Qi-Ren;CHEN Jun;DUAN Xin-Chao. An Effective Method for Improvement of Field Electron Emission Site Density and Uniformity of Amorphous Carbon Thin Films
[5]
CHAI Yang;YU Li-Gang;WANG Ming-Sheng;ZHANG Qi-Feng;WU Jin-Lei. Low-Field Emission from Iron Oxide-Filled Carbon Nanotube Arrays
[6]
GU Guang-Rui;WU Bao-Jia;JIN Feng-Xi;LI Quan-Jun;LI Zhe-Kui;ZHENG Wei-Tao;ZHAO Yong-Nian;JIN Zeng-Sun. Field Emission Characteristics of BN Films Treated with H2 and O2 Plasma
[7]
PEI Yi;ZHANG Geng-Min. Simulation of Space Charge Effect in Field Emission from a Nanowire
[8]
ZHAO Yong-Mei;ZHANG Bing-Lin;YAO Ning;LU Zhan-Ling;ZHANG Xin-Yue. Preparation of Nano-Graphite Films and Field Emission Properties
[9]
GU Guang-Rui;WU Bao-Jia;JIN Zhe;SUN Long;LI Jun-Jie;ZHAO Yong-Nian;WANG Bo;YAN Hui;WANG Wei-Biao. Field Emission Characteristics of BN Films with Cubic-BN Phase
[10]
XU Ling;HAN Guan-Qi;WENG Jian;TAM Hoi-Lam;Li King-Fai;ZHANG Yu;XU Jun;HUANG Xin-Fan;CHEAH Kok-Wai. Strong Electron Field Emission from Nano-CdS Modified Porous Silicon
[11]
LI Jun-Jie;ZHENG Wei-Tao;SUN Long;BIAN Hai-Jiao;JIN Zeng-Sun;ZHAO Hai-Feng;SONG-Hang;MENG Song-He;HE Xiao-Dong;HAN Jie-Cai. Field Emission from Amorphous Carbon Nitride Films Deposited on Silicon Tip Arrays
[12]
GU Guang-Rui;LI Ying-Ai;TAO Yan-Chun;HE Zhi;LI Jun-Jie;YIN Hong;LI Wei-Qing;ZHAO Yong-Nian;. Influence of Thickness on Field Emission Characteristics of Nanometer Boron Nitride Thin Films
[13]
HANG Lan;MA Hui-Zhong;LI Hui-Jun;YANG Shi-E;YAO Ning;HU Huan-Ling;ZHANG Bing-Lin. Nano-crystalline CNx Films and Field Electron Emission Properties
[14]
FAN Zhi-Qin;ZHANG Bing-Lin;YAO Ning;LU Zhan-Ling;YANG Shi-E;MA Bing-Xian. Controlled Growth of Carbon Nanotubes and Its Field Emission
Properties
[15]
ZHANG Geng-Min;Emmanuel ROY;LIU Hong-Wen;LIU Wei-Min;HOU Shi-Min;Kui YU-ZHANG;XUE Zeng-Quan. Field Emission from an Array of Free-standing Metallic Nanowires
1997, Vol. 14 