Direct-Current Magnetization of Y-Type Zeolites Containing Fe Ions
TONG Li-tai, WU Feng, LI Guo-hong, YAN Shou-sheng, JI Tian-hao* , LIN Bing-xiong*
Department of Physics, Peking University, Beijing 100871
* Department of Chemistry, Peking University, Beijing 100871
Direct-Current Magnetization of Y-Type Zeolites Containing Fe Ions
TONG Li-tai;WU Feng;LI Guo-hong;YAN Shou-sheng;JI Tian-hao* ;LIN Bing-xiong*
Department of Physics, Peking University, Beijing 100871
* Department of Chemistry, Peking University, Beijing 100871
关键词 :
75.20.-g ,
75.60.Ej ,
83.80.Pc
Abstract : The dc magnetization of Y-type zeolite containing Fe ions and that after reduction treatment were measured in the temperature range of 1.5-300K. The samples show paramagnetic behavior. The obtained value for the magnetic moment of the paramagnetic units strongly implies the existence of ferromagnetic coupling between the Fe ion at site I in hexagonal prism and the one at the nearest site I' in β cage.
Key words :
75.20.-g
75.60.Ej
83.80.Pc
出版日期: 1996-03-01
:
75.20.-g
(Diamagnetism, paramagnetism, and superparamagnetism)
75.60.Ej
(Magnetization curves, hysteresis, Barkhausen and related effects)
83.80.Pc
引用本文:
TONG Li-tai;WU Feng;LI Guo-hong;YAN Shou-sheng;JI Tian-hao*;LIN Bing-xiong*. Direct-Current Magnetization of Y-Type Zeolites Containing Fe Ions[J]. 中国物理快报, 1996, 13(3): 223-226.
TONG Li-tai, WU Feng, LI Guo-hong, YAN Shou-sheng, JI Tian-hao*, LIN Bing-xiong*. Direct-Current Magnetization of Y-Type Zeolites Containing Fe Ions. Chin. Phys. Lett., 1996, 13(3): 223-226.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1996/V13/I3/223
[1]
PI Li;FAN E-Hua;XIAO Ying;ZHANG Yu-Heng. Magnetic and Electrical Transport Properties of Sr1-x Lax RuO3 (0≤x≤0.10) [J]. 中国物理快报, 2006, 23(8): 2225-2228.
[2]
LIU Yao-Wen;CHEN Yu-Guang;YANG Ya-Ping;CHEN Hong;Martins J. L.. An Effective Three-Dimensional Micromagnetic Method and Its Application to Magnetic Tunnel Junctions [J]. 中国物理快报, 2005, 22(5): 1270-1273.
[3]
HOU Deng-Lu;ZHAO Jing;XU Jing;DU Zi-Xia;TANG Gui-De. Preisach Modelling on the Magnetic Properties of Nano-Particle Fe3 O4 [J]. 中国物理快报, 2005, 22(4): 946-949.
[4]
CAO Jiang-Wei;N. Katayama;YANG Zheng;WEI Fu-Lin;M. Matsumoto;A. Morisako;LIU Xiao-Xi;S. Takei. Reduction of Ordering Temperature of FePt--Al2 O3 Thin Films by N2 Addition During Sputtering [J]. 中国物理快报, 2005, 22(11): 2899-2902.
[5]
WANG Yan-Guo;WANG Hai-Ying;DAI Xue-Fang;WU Guang-Heng;DUAN Xiao-Feng. Giant Magneto-Impedance of Co50 Ni22 Ga28 Alloy with High Chemical Ordering [J]. 中国物理快报, 2005, 22(10): 2630-2632.
[6]
WANG Jian-Bo;LIU Qing-Fang;XUE De-Sheng;LI Fa-Shen. Remanence Properties and Magnetization Reversal Mechanism of Fe Nanowire Arrays [J]. 中国物理快报, 2004, 21(5): 945-948.
[7]
LI Qing-Hui;GU Dong-Hong;GAN Fu-Xi. Short-Wavelength Recording Properties of TeOx Thin Films [J]. 中国物理快报, 2004, 21(2): 320-323.
[8]
WANG Xian-Ying;ZHANG Yue-Pin;LI Zuo-Yi;SHEN De-Fang;GAN Fu-Xi. Temperature-Induced Magnetization Reorientation in GdFeCo/TbFeCo Exchange-Coupled Double Layer Films [J]. 中国物理快报, 2003, 20(8): 1359-1361.
[9]
ZHANG Yue-Pin;WANG Xian-Ying;Ruan Hao;SHEN De-Fang;GAN Fu-Xi. Annealing Effects on Properties of Bi-Substituted Garnet Films with Perpendicular Anisotropy Prepared by a Sol-Gel Method [J]. 中国物理快报, 2003, 20(5): 746-748.
[10]
WE Long;WANG Yun-Bo;WANG Hui-Yao;YUE Yong;WANG Tian-Min;ZHANG Tian-Bao;CAO Guo-Hui;. Influence of Fe in the local Structure of Perovskite Compound La2/3 Cal/3 Fel-x Mnx O3 [J]. 中国物理快报, 2000, 17(6): 446-447.
[11]
JI Yuan;CAO Guo-hui;;LI Yang;MA Qing-zhu;LI Shen;WANG Yun-bo;SHEN Bao-gen. Positron Annihilation Studies in the Sm2/3 Sr1/3 MnO3+δ [J]. 中国物理快报, 1998, 15(3): 226-227.
[12]
WANG Jifang;FISHER;E. S.;M. H. Manghnzmi. Elastic Constants of Nickel Oxide [J]. 中国物理快报, 1991, 8(3): 153-156.