Green-Light Static Rewritable Optical Storage Properties of a Novel CuTCNQ Derivative Thin Film
HUANG Wu-Qiao, WU Yi-Qun, GU Dong-Hong, GAN Fu-Xi
Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, PO Box 800-211, Shanghai 201800
Green-Light Static Rewritable Optical Storage Properties of a Novel CuTCNQ Derivative Thin Film
HUANG Wu-Qiao;WU Yi-Qun;GU Dong-Hong;GAN Fu-Xi
Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, PO Box 800-211, Shanghai 201800
关键词 :
42.70.Ln ,
78.66.-w ,
78.68.+m ,
42.62.Pc
Abstract : A novel charge-transfer complex film: copper-(n-propyl ester 7,7,8,8- tetracyanoquinodimethane-2,5-ylene-(3-propionic acid)) (Cu-TCNQ(C2 H4 COOC3 H7 )2 ) was prepared by spin-coating. Absorption spectra, green-light (514.5 nm) static rewritable optical recording properties and rewritable mechanism of this film were studied. The results show that there are two strong absorption peaks at 388 nm and 675 nm, which can be assigned to electronic transitions in anion radical TCNQ(C2 H4 COOC3 H7 )- 2 . Green-light optical storage experimental results of this film were as follows: write-in power was 9 mW, pulse duration was 80 ns; erasing power was 4 mW, pulse duration was 500 ns; the reflectivity contrast C ≥15%; number of write-erase cycle N ≥ 100. It is found that the realization of rewritable optical storage of the Cu-TCNQ (C2 H4 COOC3 H7 )2 film is related to the reversible changes of the optical properties, which is caused by the reversible charge transfer between copper and n-propyl ester 7,7,8,8- tetracyanoquinodimethane-2,5-ylene-(3-propionic acid) in the complex through inducement of laser irradiation.
Key words :
42.70.Ln
78.66.-w
78.68.+m
42.62.Pc
出版日期: 2003-12-01
:
42.70.Ln
(Holographic recording materials; optical storage media)
78.66.-w
(Optical properties of specific thin films)
78.68.+m
(Optical properties of surfaces)
42.62.Pc
引用本文:
HUANG Wu-Qiao;WU Yi-Qun;GU Dong-Hong;GAN Fu-Xi. Green-Light Static Rewritable Optical Storage Properties of a Novel CuTCNQ Derivative Thin Film[J]. 中国物理快报, 2003, 20(12): 2178-2181.
HUANG Wu-Qiao, WU Yi-Qun, GU Dong-Hong, GAN Fu-Xi. Green-Light Static Rewritable Optical Storage Properties of a Novel CuTCNQ Derivative Thin Film. Chin. Phys. Lett., 2003, 20(12): 2178-2181.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2003/V20/I12/2178
[1]
HUANG Mao-Mao;CHEN Zhi-Jian;SHI Jun;CAO Shao-Kui;GONG Qi-Huang. All-Optical Photorefractive Effect in Carbazole-Based Azo-Side Group Polymer [J]. 中国物理快报, 2006, 23(9): 2468-2471.
[2]
SUN Xi-Lian;SHAO Jian-Da. Effect of Alumina and Chromium Interlayers on Microstructures and Optical Properties of Thin Ag Films on Glass Substrates [J]. 中国物理快报, 2006, 23(9): 2576-2578.
[3]
FANG Ying-Cui;ZHANG Zhuang-Jian;SHEN Jie;LU Ming. Photoluminescence from Electron-Beam Deposited CeO2 Thin Film after High Temperature Thermal Annealing [J]. 中国物理快报, 2006, 23(7): 1919-1922.
[4]
LI Zu-Bin;TIAN Jian-Guo;ZHOU Wen-Yuan;LIU Zhi-Bo;ZANG Wei-Ping;ZHANG Chun-Ping. Highly Directional Emission from a Subwavelength Slit in Metal-Dielectric Layered Films [J]. 中国物理快报, 2006, 23(5): 1207-1210.
[5]
GAO Guo-Xiang;XU Jing-Jun;ZHANG Shu;LIU Wen-Hui;LIU Hong-De;KONG Yong-Fa;CHEN Shao-Lin;ZHANG Guang-Yin;SUN Qian. Photo-Induced Carriers in Near-Stoichiometric LiNbO3 :Fe Crystal [J]. 中国物理快报, 2006, 23(2): 443-445.
[6]
WEI Hao-Yun;CAO Liang-Cai;GU Claire;XU Zhen-Feng;HE Ming-Zhao;HE Qing-Sheng;HE Shu-Rong;JIN Guo-Fan. Holographic Grating Formation in Cationic Photopolymers with Dark Reaction [J]. 中国物理快报, 2006, 23(11): 2960-2963.
[7]
LI Guang-Ming;WAN Yu-Hong;JIANG Zhu-Qing;TAO Shi-Quan. Holographic and Thermal-Fixing Characteristics of Doubly Doped Zn:Fe:LiNbO3 Crystals [J]. 中国物理快报, 2006, 23(10): 2782-2785.
[8]
CHEN Wen-Zhong;WU Yi-Qun;WANG Yang;GAN Fu-Xi. Optical Recording Properties of Metal-Azo Dye as Recording Medium with Super-Resolution Near-Field Structure [J]. 中国物理快报, 2006, 23(1): 151-153.
[9]
ZHANG Xue-Ru. Identification of Ag37 Sn33 Te30 Phase-Change Films for Optical Data Storage [J]. 中国物理快报, 2005, 22(6): 1436-1438.
[10]
ZHAI Feng-Xiao;WANG Ai-Rong;YIN Qiong;LIU Jun-Hui;HUANG Ming-Ju;. Riboflavin Sensitized Photopolymer Materials for Holographic Storage [J]. 中国物理快报, 2005, 22(11): 2843-2846.
[11]
Raid A. Ismail;Ibrahim Ramadhan;Aseel Mustafa. Growth and Characterization of Cu2 O Films Made by Rapid Thermal Oxidation Technique [J]. 中国物理快报, 2005, 22(11): 2977-2979.
[12]
LUO Shou-Jun;LIU Guo-Dong;HE Qing-Sheng;JIN Guo-Fan. Holographic Grating Formation in Photochromic Diarylethene-Doped Polymeric Thin Films [J]. 中国物理快报, 2005, 22(1): 107-109.
[13]
SHEN Zi-Cai;KONG Wei-Jin;SHAO Jian-Da;FAN Zheng-Xiu. Modelling Analysis of Influence of Substrate Surface Defect on Optical Characteristics of Single-Layer Coating [J]. 中国物理快报, 2005, 22(1): 224-226.
[14]
YE Wei-Min;YUAN Xiao-Dong;JI Jia-Rong;ZENG Chun. Calculation of Guided Modes and Leaky Modes in Photonic Crystal Slabs [J]. 中国物理快报, 2004, 21(8): 1545-1548.
[15]
LI Qing-Hui;GU Dong-Hong;GAN Fu-Xi. Short-Wavelength Recording Properties of TeOx Thin Films [J]. 中国物理快报, 2004, 21(2): 320-323.