Mechanisms and Concentration Dependence of Upconversion Fluorescence in Er3+ and Tm3+ Codoped Tellurite Glasses
SHEN Xiang, NIE Qiu-Hua, XU Tie-Feng, PENG Tao, GAO Yuan
Faculty of Information Science and Engineering, Ningbo University, Ningbo 315211
Mechanisms and Concentration Dependence of Upconversion Fluorescence in Er3+ and Tm3+ Codoped Tellurite Glasses
SHEN Xiang;NIE Qiu-Hua;XU Tie-Feng;PENG Tao;GAO Yuan
Faculty of Information Science and Engineering, Ningbo University, Ningbo 315211
关键词 :
74.25.Gz ,
42.70.Hj ,
73.61.Jc ,
76.30.Kg
Abstract : We investigate the upconversion luminescence of Er3+ and Tm3+ codoped tellurite glasses under both the 975 and 800nm excitations. By Tm3+ codoping, the Er3+ green emission corresponding to the (4 S3/2 , 2 H11/2 ) → 4 I15/2 transitions was quenched, while the red emission corresponding to the 4 F9/2 → 4 I15/2 transition was selectively sensitized. The red emission has a maximum in the range where the ratio of Er3+ - to Tm3+ -content is about two and its fluorescence intensity becomes 1.5 and 5 times larger at the maximum than those in the absence of Tm3+ for 975 and 800nm excitations, respectively. The results were explained considering the influence of energy transfers between these two active ions.
Key words :
74.25.Gz
42.70.Hj
73.61.Jc
76.30.Kg
出版日期: 2004-12-01
引用本文:
SHEN Xiang;NIE Qiu-Hua;XU Tie-Feng;PENG Tao;GAO Yuan. Mechanisms and Concentration Dependence of Upconversion Fluorescence in Er3+ and Tm3+ Codoped Tellurite Glasses[J]. 中国物理快报, 2004, 21(12): 2507-2510.
SHEN Xiang, NIE Qiu-Hua, XU Tie-Feng, PENG Tao, GAO Yuan. Mechanisms and Concentration Dependence of Upconversion Fluorescence in Er3+ and Tm3+ Codoped Tellurite Glasses. Chin. Phys. Lett., 2004, 21(12): 2507-2510.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2004/V21/I12/2507
[1]
WU Liang-Cai;LIU Bo;SONG Zhi-Tang;FENG Gao-Ming;FENG Song-Lin;CHEN Bomy. Total Dose Radiation Tolerance of Phase Change Memory Cell with GeSbTe Alloy [J]. 中国物理快报, 2006, 23(9): 2557-2559.
[2]
WANG Xun-Si;NIE Qiu-Hua;LIU Li-Ren;XU Tie-Feng;SHEN Xiang;DAI Shi-Xun;ZHANG Xiang-Hua. Improved Fluorescence from Tm3+ /Er3+ /Ce3+ Triply Doped Bismuth-Silicate Glasses for S+C-bands Amplifiers [J]. 中国物理快报, 2006, 23(9): 2553-2556.
[3]
ZHANG Ling;ZHANG Chun-Yu;WEI Zhi-Yi;ZHANG Zhi-Guo;Stephan Strohmaier;Hans J. Eichler. Characteristics of Nd:GdVO4 Laser with Different Nd-Doping Concentrations [J]. 中国物理快报, 2006, 23(8): 2088-2091.
[4]
ZHANG Jian-Guo; WANG Xiao-Xin; CHENG Bu-Wen;YU Jin-Zhong; WANG Qi-Ming. Near Infrared Photoluminescence from Yb,Al Co-implanted SiO2 Films on Silicon [J]. 中国物理快报, 2006, 23(8): 2183-2186.
[5]
SUN Cheng-Lin;LI Jian-Fu;HU Chang-Hong;JIANG Zhan-Kui;. Optical Properties of Pr3+ -Doped Y2 SiO5 Crystals [J]. 中国物理快报, 2006, 23(7): 1915-1918.
[6]
FANG Ying-Cui;ZHANG Zhuang-Jian;SHEN Jie;LU Ming. Photoluminescence from Electron-Beam Deposited CeO2 Thin Film after High Temperature Thermal Annealing [J]. 中国物理快报, 2006, 23(7): 1919-1922.
[7]
DAI Shi-Xun;XU Tie-Feng;NIE Qiu-Hua;SHEN Xiang;WANG Xun-Si. Concentration Quenching in Erbium Doped Bismuth Silicate Glasses [J]. 中国物理快报, 2006, 23(7): 1923-1925.
[8]
WANG Chun-Yu; JI Jiang-Hua; QI Yun-Feng;LOU Qi-Hong;ZHU Xiao-Lei; LU Yu-Tian. Kilohertz Electro-Optic Q-Switched Nd:YAG Ceramic Laser [J]. 中国物理快报, 2006, 23(7): 1797-1802.
[9]
DAI Shi-Xun;ZHANG Xiang-Hua;XU Tie-Feng;SHEN Xiang;WANG Xun-Shi;NIE Qiu-Hua. High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses [J]. 中国物理快报, 2006, 23(7): 1810-1812.
[10]
CHEN Feng;WANG Xue-Lin;WANG Ke-Ming;WANG Lei;JIAO Yang;WANG Liang-Ling;LU Qing-Ming;MA Hong-Ji;NIE Rui. Optical Planar Waveguides in KTiOPO4 Crystals by MeV Oxygen Ion Implantation [J]. 中国物理快报, 2006, 23(6): 1501-1503.
[11]
WANG Xiao-Xin;ZHANG Jian-Guo;CHENG Bu-Wen;YU Jin-Zhong;WANG Qi-Ming. Electroluminescence Afterglow from Indium Tin Oxide/Si-Rich SiO2 /p-Si Structure [J]. 中国物理快报, 2006, 23(5): 1306-1309.
[12]
JIANG Yi;WANG Ke-Ming;WANG Xue-Lin;JIA Chuan-Lei;ZHANG Jian-Xiu;WANG Ji-Yang;MA Hong-Ji;NIE Rui;SHEN Ding-Yu. Optical Waveguide Formed in Yb:KLu(WO4 )2 Crystal by 6.0MeV O+ Implantation [J]. 中国物理快报, 2006, 23(4): 922-924.
[13]
ZHOU Rui;DING Xin;WEN Wu-Qi;CAI Zhi-Qiang;WANG Peng;YAO Jian-Quan. High-Power Continuous-Wave Diode-End-Pumped Intracavity Frequency Doubled Nd:YVO4 Laser at 671nm with a Compact Three-Element Cavity [J]. 中国物理快报, 2006, 23(4): 849-851.
[14]
XU Shi-Qing;FENG Ai-Ming;ZHANG Li-Yan;ZHAO Shi-Long;WANG Bao-Ling;ZHANG Jue;WANG Wei;BAO Ren-Qiang. Thermal Stability and Spectroscopic Properties of Yb3+ -Doped New Gallium--Lead--Germanate Glass [J]. 中国物理快报, 2006, 23(11): 3069-3071.
[15]
ZHOU Shi-Feng;FENG Gao-Feng;XU Shi-Qing;WU Bo-Tao;QIU Jian-Rong. Broadband Near-Infrared Emission from Transparent Ni2+ -Doped Sodium Aluminosilicate Glass Ceramics [J]. 中国物理快报, 2006, 23(11): 2996-2998.