Serrated Plastic Flow in a Zr-based Bulk Metallic Glass During Nanoindentation
DAI Lan-Hong1;LIU Long-Fei1;YAN Min1;WEI Bing-Chen2;ECKERT Jürgen3
State Key Laboratory of Nonlinear Mechanics (LNM), Institute of Mechanics, Chinese Academy of Sciences, Beijing 100080
National Microgravity Laboratory, Institute of Mechanics, Chinese Academy of Sciences, Beijing 100080
Department of Materials and Geosciences, Physical Metallurgy Division, Darmstadt University of Technology, Petersenstr 23, D-64287 Darmstadt, Germany
Abstract: We investigate plastic deformation of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass using depth sensing nanoindentation. Numerous serrations in the load-displacement curves during indentation, shear bands and pile-ups around the indent were observed. The results revealed that the serrated
plastic flow behaviour in this alloy depends strongly on the indentation strain rate.