Structural and Magnetic Properties of Tb(Fel-xNix)11.3Nb0.7 Compounds
WANG Jian-li1, YANG Fu-ming1, BAO Fu-quan1, TANG Ning1,2, HAN Xiu-feng1, YANG Dong1, ZHANG Cheng2, F. R. de Boer2
1State Key Laboratory of Magnetism, Institute of Physics, Chinese Academy of Sciences, Beijing 100080
2Van der Waals-Zeeman Institute, University of Amsterdam, Valckenierstraat 65, 1018 XE Amsterdam, The Netherlands
Structural and Magnetic Properties of Tb(Fel-xNix)11.3Nb0.7 Compounds
WANG Jian-li1;YANG Fu-ming1;BAO Fu-quan1;TANG Ning1,2;HAN Xiu-feng1;YANG Dong1;ZHANG Cheng2;F. R. de Boer2
1State Key Laboratory of Magnetism, Institute of Physics, Chinese Academy of Sciences, Beijing 100080
2Van der Waals-Zeeman Institute, University of Amsterdam, Valckenierstraat 65, 1018 XE Amsterdam, The Netherlands
Abstract： Structural and magnetic properties of Tb(Fel-xNix)11.3Nb0.7 compounds have been investigated. The x-ray diffraction patterns show that all compounds crystallize in the ThMn12-type structure and that all samples are almost of single phase. The lattice constants monotonously decrease with increasing Ni content. The Curie temperature Tc clearly increases and the saturation moment Ms monotonously decreases with increasing Ni content. X-ray diffraction patterns of aligned samples at room temperature show that for x ≤ 0.2 the easy magnetization direction is in the plane while for the x = 0.25 compound the easy magnetization direction is along the c-axis. In the compounds with x ≤ 0.20 spin reorientation occurs above room temperature whereas in the compounds with x > 0.2 there is a spin reorientation below room temperature. It has been found that Ni contributes positively to the T-sublattice moment MT.
WANG Jian-li;YANG Fu-ming;BAO Fu-quan;TANG Ning;HAN Xiu-feng;YANG Dong;ZHANG Cheng;F. R. de Boer. Structural and Magnetic Properties of Tb(Fel-xNix)11.3Nb0.7 Compounds[J]. 中国物理快报, 1998, 15(12): 922-924.
WANG Jian-li, YANG Fu-ming, BAO Fu-quan, TANG Ning, HAN Xiu-feng, YANG Dong, ZHANG Cheng, F. R. de Boer. Structural and Magnetic Properties of Tb(Fel-xNix)11.3Nb0.7 Compounds. Chin. Phys. Lett., 1998, 15(12): 922-924.
1998, Vol. 15 