Positron Annihilation During Pre-crystallizat ion Process in an Amorphous Silver Ionic Conductor
CAO Shixun*, CHEN Liquan**, XUE Rongjian**, HE Yusheng, YU Weizhong
*Department of Physics, Henan Normal University, Xinxiang 453002
**Institute of Physics, Academia Sinica, Beiing 100080
Department of Physics, Tsinghua University, Beijing 100084
Positron Annihilation During Pre-crystallizat ion Process in an Amorphous Silver Ionic Conductor
CAO Shixun*;CHEN Liquan**;XUE Rongjian**;HE Yusheng;YU Weizhong
*Department of Physics, Henan Normal University, Xinxiang 453002
**Institute of Physics, Academia Sinica, Beiing 100080
Department of Physics, Tsinghua University, Beijing 100084
Abstract: The study of positron annihilation on amorphous 0.60AgI-O.25Ag2O-0.15P2O5 has been carried out in the temperature range from 100 to 350K. The temperature dependence of average lifetime shows anomalous peaks at 208, 228, 325, 338 K indicating possible structure relaxation. Especially the last two peaks reflect the structural changes during pre-crystallization process of the amorphous ionic conductor. These results are consistent with that of ultrasonic attenuation and ionic conductivity experiments on the same samples.
CAO Shixun*;CHEN Liquan**;XUE Rongjian**;HE Yusheng;YU Weizhong. Positron Annihilation During Pre-crystallizat ion Process in an Amorphous Silver Ionic Conductor[J]. 中国物理快报, 1993, 10(1): 37-40.
CAO Shixun*, CHEN Liquan**, XUE Rongjian**, HE Yusheng, YU Weizhong. Positron Annihilation During Pre-crystallizat ion Process in an Amorphous Silver Ionic Conductor. Chin. Phys. Lett., 1993, 10(1): 37-40.