Fabrication and Mossbauer Study of FeCo Alloy Nanotube Array
ZHOU Dong;LI Zhi-Wei;YANG Xu;WEN Fu-Sheng;LI Fa-Shen
Institute of Applied Magnetics, Key Laboratory for Magnetism and Magnetic Materials of the Ministry of Education, Lanzhou University, Lanzhou 730000
Cite this article:   
ZHOU Dong, LI Zhi-Wei, YANG Xu et al  2008 Chin. Phys. Lett. 25 1865-1867
Download: PDF(824KB)  
Export: BibTeX | EndNote | Reference Manager | ProCite | RefWorks
Abstract Arrays of FeCo nanotubes are fabricated in the pores of porous anodic aluminium oxide templates. Transmission electron microscopic result shows that the nanotubes are regular and uniform. Magnetic hysteresis loops measured at room temperature are different from those of nanowires with the same composition, which are caused by the unique shape of nanotubes. The Mossbauer spectra show that the hyperfine field is smaller than that of the bulk's and increases with decrease of measuring temperature. However, the areas of the doublets appeared in Mossbauer spectra decrease with
decrease of measuring temperature.
Keywords: 75.50.Bb. 75.75.+a     
Received: 28 January 2008      Published: 29 April 2008
PACS:  75.50.Bb. 75.75.+a  
TRENDMD:   
URL:  
https://cpl.iphy.ac.cn/       OR      https://cpl.iphy.ac.cn/Y2008/V25/I5/01865
Service
E-mail this article
E-mail Alert
RSS
Articles by authors
ZHOU Dong
LI Zhi-Wei
YANG Xu
WEN Fu-Sheng
LI Fa-Shen
[1] Yu R H, Ren L, Basu S, Unruh K M, A. Parvizi-Majidi andXiao J Q 2000 J. Appl. Phys. 87 5840
[2] Dong X L, Zhang Z D, Jin S R and Kim B K 2000 J.Magn. Magn. Mater. 210 143
[3] Zhan Q F, Chen Z Y, Xue D S, Li F S, Kunkel H, Zhou X Z,Roshko R and Williams G 2002 Phys. Rev. B 66 134436
[4] Chen Z Y, Zhan Q F, Xue D S, Li F S, Zhou X Z, Kunkel Hand Williams G 2002 J. Phys.: Condens. Matter 14 613
[5] Matthias B and Gatzen H H 2006 J. Appl. Phys. 99 08M308
[6] Gasparac R, Kohli P, Mota M O, Trofin L and Martin C R2004 Nano Lett. 4 513
[7] Khizroev S, Kryder M H, Litvinov D, and Thompson D A 2002 Appl. Phys. Lett. 81 2256
[8] Sui Y C, Skomski R, Sorge K D and Sellmyer D J 2004 J. Appl. Phys. 95 7151
[9] Bao J C, Tie C Y, Xu Z, Zhou Q F, Shen D and Ma Q 2001 Adv. Mater. 13 1631
[10] Masuda H and Fukuda K 1995 Science 268 1466
[11] Preston R S, Hanna S S and Heberle J 1962 Phys.Rev. 128 2207
[12] Li F S, D. Zhou, Wang T, Wang Y, Song L J and Xu C T 2007 J. Appl. Phys. 101 014309
[13] M{\orup S 1983 J Magn. Magn. Mater. 37 39
[14] Lataifeh M S 2000 J. Phys. Soc. Jpn. 69 248
[15] Zhang X X 2005 Handbook of Advanced MagneticMaterials (Beijing: Tsinghua University Press) vol 1
Viewed
Full text


Abstract