Chin. Phys. Lett.  1995, Vol. 12 Issue (8): 465-468    DOI:
Original Articles |
Stable Mg- Zn-Y Quasicrystals
LUO Zhiping1,2;ZHANG Shaoqing1;ZHAO Dongshan3;TANG Yali3;SUI Haixin2
1Beijing Institute of Aeronautical Materials, Beijing 100095 2Beijing Laboratory of Electron Microscopy, Academia Sinica, P. O. Box 2724, Beijing 100080 3Zhengzhou Institute of Technology, Zhengzhou 450002
Cite this article:   
LUO Zhiping, ZHANG Shaoqing, ZHAO Dongshan et al  1995 Chin. Phys. Lett. 12 465-468
Download: PDF(152KB)  
Export: BibTeX | EndNote | Reference Manager | ProCite | RefWorks
Abstract By conventional air-cooled casting method, cast ingots with large contents of stable Mg-Zn-Y quasicrystals were obtained. It was shown that most of the quasicrystals are of face-centered icosahedral type, while a few of them belong to simple icosahedral type. The quasicrystals were stable during the continuous heating with the temperature below 868K. The oxidizing reactions were observed at high temperature. This is the characteristic of Mg-Zn-Y alloys, which differs from that of A1 base alloys.
Keywords: 61.44.+p      61.55.-x     
Published: 01 August 1995
PACS:  61.44.+p  
  61.55.-x  
TRENDMD:   
URL:  
https://cpl.iphy.ac.cn/       OR      https://cpl.iphy.ac.cn/Y1995/V12/I8/0465
Service
E-mail this article
E-mail Alert
RSS
Articles by authors
LUO Zhiping
ZHANG Shaoqing
ZHAO Dongshan
TANG Yali
SUI Haixin
Related articles from Frontiers Journals
[1] LI Xian-fang, FAN Tian-you. New Method for Solving Elasticity Problems of Some Planar Quasicrystals and Solutions[J]. Chin. Phys. Lett., 1998, 15(4): 465-468
[2] LI Fang-hua, CHENG Yi-fan. Relationship Between Octagonal Quasicrystal and β-Mn Type Crystal in Cut Description[J]. Chin. Phys. Lett., 1996, 13(3): 465-468
Viewed
Full text


Abstract